Primers and a method of coating in which they are used
Disclosed is a primer having from 50 to 90 mass % of (A) a chlorinated polyolefin resin having a chlorine content of from 5 to 50 mass % and a weight average molecular weight of from 1,000 to 100,000, from 45 to 5 mass % of (B) a blocked polyisocyanate compound, from 45 to 5 mass % of (C) a polyol resin having a hydroxyl group value of from 30 to 120 mgKOH/g and a weight average molecular weight from 5,000 to 50,000, from 0.5 to 12 mass % of (D) a diol having a weight average molecular weight of from 120 to 1,000 and from 0.01 to 1.5 mass % of (E) a hardening catalyst, wherein the proportions are with respect to the total mass of the resin solid fraction of the (A), (B), and (C) components.
1. A primer, comprising:
(A) from 50 to 90 mass % of a chlorinated polyolefin resin comprising a chlorine content of from 5 to 50 mass % and a weight average molecular weight of from 1,000 to 100,000,
(B) from 45 to 5 mass % of a blocked polyisocyanate compound,
(C) from 45 to 5 mass % of a polyol resin comprising a hydroxyl group value of from 30 to 120 mgKOH/g and a weight average molecular weight of from 5,000 to 50,000,
(D) from 0.5 to 12 mass % of a diol comprising a weight average molecular weight from 120 to 1,000 and
(E) from 0.01 to 1.5 mass % of a hardening catalyst,
wherein the mass % proportions are based on the total mass of resin solid fractions of (A), (B) and (C).
2. A method of coating a molding, comprising:
sequentially coating the primer of claim 1 and a top-coat paint on a molding; and
baking and hardening the applied primer and top-coat paint to form a top-coat paint film.
3. The method of claim 2 , wherein the top-coat paint is a one-coat, two-liquid urethane resin paint.
4. The method of claim 2 , wherein the top-coat paint film comprises a base-coat paint film and a clear paint film, and at least the clear paint film is obtained by the baking and hardening of a two-liquid, urethane resin paint.
5. The method of claim 2 , wherein the top-coat paint film comprises a colored base-coat paint film, a pearl base-coat paint film and a clear paint film, and at least the clear paint film is obtained by the baking and hardening of a two-liquid, urethane resin paint.
6. The method of claim 2 , wherein the molding is comprised of plastic.
7. A method of coating a molding comprising:
sequentially coating the primer of claim 1 and a top-coat paint on a molding;
baking and hardening the applied primer and top-coat paint to form a top-coat paint film;
sequentially coating the primer of claim 1 and the top-coat paint onto the top-coat paint film; and
baking and hardening the applied primer and top-coat paint.
8. A primer, comprising
(A) from 60 to 80 mass % of a chlorinated polyolefin resin comprising a chlorine content of from 18 to 25 mass % and a weight average molecular weight of from 10,000 to 80,000,
(B) from 30 to 10 mass % of a blocked polyisocyanate compound,
(C) from 30 to 10 mass % of a polyol resin comprising a hydroxyl group value of from 40 to 70 mgKOH/g, an acid value of from 0 to 25 mg KOH/g, and a weight average molecular weight of from 7,000 to 20,000,
(D) from 1.5 to 8 mass % of a diol comprising a weight average molecular weight from 120 to 800 and
(E) from 0.05 to 0.8 mass % of a hardening catalyst comprising at least one of a tin compound or a zinc compound,
wherein the mass % proportions are based on the total mass of resin solid fractions of (A), (B) and (C).