Conversion of just-continuous metallic films to large particulate substrates for metal-enhanced fluorescence
The present invention relates to a method of producing silver films having large nanoparticles caused by cracking during anaerobic annealing to provide surfaces that exhibit increased metal enhanced fluorescence. Preferably the annealing process is conducted on a silver film having a thickness from about 14 to 17 nm for about an hour at a temperature of approximately 190° C. to about 210° C. resulting in the conversion of the just-continuous films into large particulate films, not readily assessable by other chemical deposition techniques.
1. A method of fabricating a cracked surface that includes a plurality of nanoparticles having a cross-sectional diameter from about 60 nm to about 150 nm and a thin silver film layer less than the height of the nanoparticles positioned between the nanoparticles, the method comprising:
providing a substrate;
depositing a 12 nm to about 17 nm continuous layer of silver on the substrate to form a just continuous silver film coating the substrate;
heating the silver film and substrate to a temperature of from about 170° C. to about 230° C. under anaerobic conditions for about 0.5 to 2.5 hours to provide crackage in the silver film thereby forming annealed nanoparticles having a cross-sectional diameter from about 60 nm to about 150 nm and a thin silver film layer remaining between the nanoparticles having a thickness less than the unannealed deposited layer of silver,
wherein the annealed nanoparticles provide for increased metal enhanced fluorescence relative to an unannealed film.
2. The method of claim 1 , wherein the surface substrate is glass, quartz, polymeric material or a metallic surface not including silver.
3. The method of claim 1 , wherein the annealing temperature is from about 190° C. to about 210° C.
4. The method of claim 1 , wherein the annealed nanoparticles have a surface plasmon resonance (SPR) peak that is blue shifted relative to the unannealed surface.
5. A detection method exhibiting increased fluorescence emitted during metal-enhanced fluorescence sensing, the detection method comprising:
applying a metallic material to a surface substrate used in a detection system to form individual nanoparticles having a cross-sectional diameter from about 60 nm to about 150 nm and a thin silver film layer less than the height of the nanoparticles positioned between the nanoparticles, wherein the metallic material is formed by:
providing a substrate;
depositing a 12 to 17 nm thick continuous layer of silver on the substrate to form a continuous silver film coating the substrate;
heating the silver film and substrate to a temperature of about 190° C. to 210° C. under anaerobic conditions for a sufficient amount of time to form annealed nanoparticles and a thin silver film layer remaining between the nanoparticles having a thickness less than the unannealed deposited layer of silver;
providing a an intrinsic or extrinsic fluorophore for disposing near the annealed nanoparticles,
exciting the fluorophore with an electromagnetic source to cause fluorescing; and
measuring the fluorescence emission within the fluorophore and/or annealed nanoparticles.
6. The detection method according to claim 5 , further comprising the step of applying electromagnetic energy in the microwave range to cause an increase in heat in the system thereby increasing the kinetics of any chemical reactions occurring within the detection system.
7. The method of claim 5 , wherein the heating period is about 0.5 to 2.5 hours.
8. The method of claim 5 , wherein the heating period is about 1 hour.
9. The method of claim 5 wherein the thickness of the deposited silver film layer, before annealing, is from about 14 nm to 16 nm thick.
10. The method of claim 5 , wherein the annealed nanoparticles have a surface plasmon resonance (SPR) peak that is blue shifted relative to the unannealed surface.
11. A cracked silver surface that comprises individual nanoparticles having a cross-sectional diameter from about 60 nm to about 150 nm; and
a thin silver film layer less than the height of the nanoparticles and positioned between the nanoparticles, wherein the cracked silver surface is fabricated by a method comprising:
providing a substrate;
depositing a 12 to 17 nm thick continuous layer of silver on the substrate to form a silver coated substrate; and
heating the silver coated substrate to a temperature of about 190° C. to 210° C. under anaerobic conditions for a time period of about 0.5 to 2.5 hours to provide crackage in the silver film thereby forming annealed nanoparticles having a cross-sectional diameter from about 60 nm to about 150 nm and a thin silver film layer remaining between the nanoparticles having a thickness less than the unannealed deposited layer of silver,
wherein the annealed nanoparticles provide for increased metal enhanced fluorescence relative to an unannealed film.
12. The silver biosensor surface of claim 11 , wherein the annealed nanoparticles include a height greater than the thickness of the unannealed deposited layer of silver, whereby the silver is conserved and redistributed during the annealing process.
13. The silver biosensor surface of claim 11 , wherein the annealing is conducted in about one hour.
14. The silver biosensor surface of claim 11 , wherein the thickness of the deposited silver film layer, before annealing, is from about 14 nm to 16 nm thick.
15. The silver biosensor surface of claim 11 , wherein the annealed nanoparticles have a surface plasmon resonance (SPR) peak that is blue shifted relative to the unannealed surface.
16. The silver biosensor surface of claim 11 , wherein the surface substrate is glass, quartz, polymeric material or a metallic surface not including silver.
17. The silver biosensor surface of claim 11 , further comprising the step of applying electromagnetic energy in the microwave range to cause an increase in heat in the system thereby increasing the kinetics of any chemical reactions occurring within the detection system.