This invention relates to protective, multi-layered, breathable fabric constructs. The constructs which are flexible employ a fabric layer and a breathable coating layer applied to the fabric. Under certain preferred embodiments, the fabric constructs also employ an energy dissipating fiber material disposed opposite the coating layer. Also, the present invention teaches a method of protecting a valuable or sensitive object from damage caused by corrosion, weather, bio mass, or other environmental related conditions using the fabric material. The fabric constructs may be post-formed using heat or other methods to create shaped-to-form covers.
1. A method of manufacturing substantially waterproof moisture vapor permeable cover material comprising the step of:
a. providing a hydrophilic fabric layer comprising a nonwoven material, or a combination of woven and non-woven materials, including two layers with an inner layer of lower hydrophilicity and an outer layer of greater hydrophilicity;
b. applying an adhesive to the fabric layer;
c. applying flocked fibers to the adhesive layer to form an inner side of the cover material designed to contact an item to be covered; and
d. extrusion coating a substantially waterproof, moisture vapor permeable polymeric top layer to the fabric layer on the side opposite the adhesive and flocked fibers to form an outer side of the cover material configured to be exposed to an external environment, and said moisture vapor permeable polymeric top layer being extruded on said fabric, the outer layer of fabric being adjacent the moisture vapor permeable polymeric top layer.
2. The method of claim 1 wherein said adhesive layer is formed from a water or solvent based adhesive composition selected from one or more of the group consisting of acrylic latexes, urethanes, and epoxies.
3. The method of claim 1 comprising applying said adhesive by spray coating, knife coating, curtain coating, reverse roll coating, gravure coating or rotary screen coating.
4. The method of claim 1 wherein said adhesive layer is formed from an intumescent adhesive composition.
5. The method of claim 2 wherein said adhesive is hydrophilic and contains vapor corrosion inhibitors.
6. The method of claim 2 wherein said adhesive is modified with titanates and/or zirconates.
7. The method of claim 2 wherein said adhesive layer further comprises one or more additives selected from the group consisting of vapor corrosion inhibitors, anti-static agents, antimicrobials and biostatics.
8. The method of claim 1 wherein said adhesive layer is foamed.
9. The method of claim 1 wherein said flocked fibers are electro-statically and mechanically applied to said adhesive.
10. The method of claim 1 wherein said flocked fibers comprise one or more materials selected from rayon, acetate, nylon, polyolefin, acrylic, polyester, carbon fiber, cotton, hemp, and wool.
11. The method of claim 1 wherein said flocked fibers have an average denier of 0.5 to 90 deniers.
12. The method of claim 1 wherein said flocked fibers have an average length between 0.25 mm and 20.0 mm.
13. The method of claim 1 wherein said substantially waterproof, moisture vapor permeable polymer composition comprises a fatty acid modified ionomer at least partially neutralized with potassium ions and/or sodium ions.
14. The fabric construct of claim 1 wherein the moisture vapor permeable polymeric composition comprises a polyamide/polyether block copolymer.
15. The method of claim 1 wherein the moisture vapor permeable polymeric composition comprises a potassium salt of a fatty acid and an ionomer comprising a plurality of carboxylate groups.
16. The method of claim 1 wherein the moisture vapor permeable polymeric composition forms a layer having an average thickness of 0.5 mil to 10 mils.
17. The method of claim 1 wherein the moisture vapor permeable polymeric composition forms a layer having a water vapor transmission rate of at least 100 grams/square meter/day at 37.8° C. and 100% relative humidity.
18. The method of claim 1 further including a woven scrim between said layers of fabric.
19. The method of claim 18 including the step of entangling said layers of fabric with the said scrim.