Titania-graphene anode electrode paper
A method for forming a nanocomposite material, the nanocomposite material formed thereby, and a battery made using the nanocomposite material. Metal oxide and graphene are placed in a solvent to form a suspension. The suspension is then applied to a current collector. The solvent is then evaporated to form a nanocomposite material. The nanocomposite material is then electrochemically cycled to form a nanocomposite material of at least one metal oxide in electrical communication with at least one graphene layer.
1. A method for forming a nanocomposite material comprising the steps of:
dispersing qraphene with a surfactant forming a first mixture;
providing a metal oxide in an aqueous solution to form a second mixture;
adding the second mixture to the first mixture to form a metal oxide and qraphene nanocomposite;
adding the metal oxide and graphene nanocomposite to a solvent to form a suspension;
applying the suspension to a current collector; and
evaporating the solvent to form a dried metal oxide and graphene nanocomposite material wherein the metal oxide is in electrical communication with at least one graphene layer.
2. The method of claim 1 wherein the solvent is an organic solvent.
3. The method of claim 1 wherein the metal oxide is titania.
4. The method of claim 1 wherein the titania is provided as particles having an average diameter below 50 nm.
5. The method of claim 1 wherein the titania is provided as particles having an average diameter below 10 nm.
6. A method for forming a nanocomposite material comprising the steps of:
dispersing graphene with a surfactant forming a first mixture;
providing an aqueous second mixture of metal oxide;
adding the second mixture to the first mixture to form a metal oxide and graphene nanocomposite;
adding the metal oxide and graphene nanocomposite to solvent to form a suspension, applying the suspension to a current collector,
evaporating the solvent to form an anode,
connecting the anode to a cathode having lithium ions and an electrolyte to form a battery, and
electrochemically cycling the anode to form a nanocomposite material comprising at least one metal oxide in electrical communication with at least one graphene layer.
7. The method of claim 6 wherein the solvent is an organic solvent.
8. The method of claim 6 wherein the metal oxide is titania.
9. The method of claim 6 wherein the titania is provided as particles having an average diameter below 50 nm.
10. The method of claim 6 wherein the titania is provided as particles having an average diameter below 10 nm.
11. A method for forming a nanocomposite material comprising:
dispersing graphene with a surfactant to form a first mixture;
mixing titanium dioxide and water to form a second mixture;
combining the second mixture into the first mixture to form a suspension;
filtering the suspension and calcining the residue to form a titanium dioxide and graphene nanocomposite material wherein the titanium dioxide is in electrical communication with at least one graphene layer;
mixing the titanium dioxide and graphene nanocomposite material with a solvent to form a slurry;
applying the slurry to a current collector; and
evaporating the solvent to form an anode.
12. The method of claim 11 wherein the solvent comprises an organic solvent.
13. The method of claim 11 wherein the solvent comprises poly(tetrafluoroethylene).
14. The method of claim 11 wherein the surfactant comprises cetyl trimethylammonium bromide.
15. The method of claim 11 wherein the ratio of titanium dioxide to graphene in the titanium dioxide and graphene nanocomposite material is from about 72/28 wt % to about 90/10 wt %.
16. The method of claim 1 wherein the ratio of titanium dioxide to graphene in the titanium dioxide and graphene nanocomposite material is from about 72/28 wt % to about 90/10 wt %.