Ni-25 heat-resistant nodular graphite cast iron for use in exhaust systems
A nodular graphite, heat-resistant cast iron composition for use in engine systems. The composition contains carbon 1.5-2.4 weight %, silicon 5.4-7.0 weight %, manganese 0.5-1.5 weight %, nickel 22.0-28.0 weight %, chromium 1.5-3.0 weight %, molybdenum 0.1-1.0 weight %, magnesium 0.03-0.1 weight %, and a balance weight % being substantially iron. The composition has an austenitic matrix. Additionally, the composition exhibits excellent oxidation resistance at high temperature and excellent mechanical properties at both room and high temperatures. Thus, the composition can be a lower cost substitute material for Ni-Resist D5S under thermocycling conditions experienced by exhaust gas accessories and housings such as engine exhaust manifolds, turbocharger housings, and catalytic converter housings.
1. A heat resistant, nodular graphite cast iron composition consisting essentially of carbon 1.5-2.4 weight %, silicon 5.4-7.0 weight %, manganese 0.5-0.69 weight %, nickel 25.2-28.0 weight %, chromium 1.5-2.04 weight %, molybdenum 0.1-1.0 weight %, magnesium 0.03-0.1 weight %, and the balance weight % being iron and incidental elements and impurities.
2. A composition as set forth in claim 1 consisting essentially of carbon 1.88 weight %, silicon 5.85 weight %, manganese 0.69 weight %, nickel 25.2 weight %, chromium 2.04 weight %, molybdenum 0.12 weight %, magnesium 0.065 weight %, and the balance weight % being iron and incidental elements and impurities.
3. An engine system ( 12 ) comprising;
an engine ( 14 ) for generating an exhaust gas,
an exhaust gas accessory ( 16 ) in fluid communication with said engine ( 14 ) for receiving or containing the exhaust gases from said engine ( 14 ),
wherein said exhaust gas accessory ( 16 ) at least in part consists essentially of carbon 1.5-2.4 weight %, silicon 5.4-7.0 weight %, manganese 0.5-0.69 weight %, nickel 25.2-28.0 weight %, chromium 1.5-2.04 weight %, molybdenum 0.1-1.0 weight %, magnesium 0.03-0.1 weight %, and the balance weight % being iron and incidental elements and impurities.
4. A system ( 12 ) as set forth in claim 3 , wherein said exhaust gas accessory ( 16 ) at least in part consists essentially of carbon 1.88 weight %, silicon 5.85 weight %, manganese 0.69 weight %, nickel 25.2 weight %, chromium 2.04 weight %, molybdenum 0.12 weight %, magnesium 0.065 weight %, and the balance weight % being iron and incidental elements and impurities.