Cast iron alloy for cylinder heads
A lamellar graphite cast iron alloy is described which, as additives, has 2.80% by weight-3.60% by weight carbon (C), 1.00% by weight-1.70% by weight silicon (Si), 0.10% by weight-1.20% by weight manganese (Mn), 0.03% by weight-0.15% by weight sulphur (S), 0.05% by weight-0.30% by weight chromium (Cr), 0.05% by weight-0.30% by weight molybdenum (Mo), 0.05% by weight-0.20% by weight tin (Sn) and the usual impurities, and also described is a cylinder head which can be obtained therefrom.
1. A lamellar graphite cast iron alloy, characterized in that the cast iron alloy has as additives
2.80% by weight-3.60% by weight carbon (C),
1.00° A) by weight-1.70% by weight silicon (Si),
0.10% by weight-1.20% by weight manganese (Mn),
0.03% by weight-0.15% by weight sulphur (S),
0.05% by weight-0.30% by weight chromium (Cr),
0.05% by weight-0.30% by weight molybdenum (Mo),
0.05% by weight-0.20% by weight tin (Sn)
and the usual impurities; and
wherein a matrix of a structure of the cast iron alloy is constructed from pearlite with at most about 5% ferrite.
2. The cast iron alloy according to claim 1 , characterized in that silicon (Si) is present in a quantity of 1.00% by weight to 1.50% by weight.
3. A lamellar graphite cast iron alloy characterized in that the cast iron alloy has, as additives
3.20% by weight-3.50% by weight carbon (C),
1.30% by weight-1.50% by weight silicon (Si),
0.50% by weight-0.60% by weight manganese (Mn),
0.08% by weight-0.12% by weight sulphur (S),
0.10% by weight 0.15% by weight chromium (Cr),
0.20% by weight-0.25% by weight molybdenum (Mo),
0.05% by weight-0.10% by weight tin (Sn)
and the usual impurities; and
wherein a matrix of a structure of the cast iron alloy is constructed from pearlite with at most about 5% ferrite.
4. The cast iron alloy according to anyone of the preceding claims, characterized in that of the usual impurities the following are present: up to 1% by weight nickel (Ni), up to 1% by weight copper (Cu), up to 0.2% by weight titanium (Ti), up to 0.2% by weight vanadium (V), up to 0.2% by weight niobium (Nb), up to 0.03% by weight nitrogen (N) and up to 0.15% by weight phosphorus (P).
5. The cast iron alloy according to claim 1 or 3 , characterized in that the lamellar graphite in a particle is present in form I, with more than 80% in arrangement A and in size 3 or finer (EN ISO 945:1994-09).
6. The cast iron alloy according to claim 1 or 3 , obtainable by inoculation with 0.0005% by weight to 0.0500% by weight barium.
7. A cylinder head, cast from the cast iron alloy according to claims 1 or 3 .
8. The cylinder head according to claim 7 , characterized in that the cylinder head is of an internal combustion engine.
9. The cylinder head according to claim 7 , characterized in that the cylinder is configured as a series cylinder head for a multi-cylinder engine.
10. The cylinder head according to either of claim 8 , characterized in that the cylinder is configured as a series cylinder head for a multi-cylinder engine.
11. The cast iron alloy according to claim 6 obtainable by inoculation with 0.0010% by weight to 0.00125% by weight barium.
12. A lamellar graphite cast iron alloy component, characterized in that the cast iron alloy has the following constituents:
2.80% by weight-3.60% by weight carbon (C),
1.00% by weight-1.70% by weight silicon (Si),
0.10% by weight-1.20% by weight manganese (Mn),
0.03% by weight-0.15% by weight sulphur (S),
0.05% by weight-0.30% by weight chromium (Cr),
0.05% by weight-0.30% by weight molybdenum (Mo),
0.05% by weight-0.20% by weight tin (Sn)
and usual impurities, the balance iron,
wherein the matrix of the structure of the component from the cast iron alloy is constructed from pearlite with at most about 5% ferrite.