Graft compositions, useful for tie-layer adhesives, are disclosed. The graft compositions comprise the reaction product of a live, grafted polyolefin and an olefin elastomer. The grafted polyolefin is first made by heating a polyolefin and an unsaturated monomer. Further reaction of the live, grafted polyolefin with an olefin elastomer provides the graft composition. Grafting efficiency is boosted dramatically by the presence of the olefin elastomer and use of the additional reaction step. The graft composition, when formulated into a tie-layer adhesive at low concentration, affords multilayer structures with good adhesion and high clarity.
1. A composition comprising:
a graft (polyolefin/elastomer) copolymer wherein the copolymer comprises:
(i) a grafted polyolefin; and,
(ii) an olefin elastomer
wherein the graft (polyolefin/elastomer) copolymer is produced by a radical coupling reaction between a live, grafted polyolefin and the olefin elastomer.
2. The composition of claim 1 wherein the grafted polyolefin is high-density polyethylene (HDPE) grafted with maleic anhydride.
3. The composition of claim 1 wherein the olefin elastomer is ethylene-propylene rubber (EPR) or ethylene-propylene-diene monomer rubber (EPDM).
4. The composition of claim 1 which exhibits an infrared absorption in the range of 1725 to 1735 cm −1 .
5. The composition of claim 1 comprising:
2 to 50 wt. % of the graft (polyolefin/elastomer) copolymer and 50-98 wt. % of a resin.
6. The composition of claim 5 comprising:
5 to 30 wt. % of the graft (polyolefin/elastomer) copolymer and 70 to 95 wt. % of the resin.
7. The composition of claim 6 wherein the grafted polyolefin is a maleic anhydride-grafted polyethylene, and the resin comprises a LLDPE.
8. The composition of claim 5 wherein the grafted polyolefin is a maleic anhydride-grafted polyethylene, and the resin is ethylene-vinyl acetate (EVA) copolymer.
9. The composition of claim 5 wherein the resin comprises at least one compound selected from the group consisting of: an ethylene homopolymer; a copolymer of ethylene with C 3 -C 8 α-olefins; a vinyl carboxylate; an alkyl acrylate; a terpolymer of ethylene and propylene with diene monomers; a propylene homopolymer; a polyisobutylene; a copolymer of isobutylene; and a copolymer of isoprene.
10. The composition of claim 9 wherein the resin comprises at least one compound selected from the group consisting of a LDPE, a MDPE, a HDPE, a LLDPE, a very low density polyethylene, an ultra-low density polyethylene, and blends thereof.
11. The composition of claim 9 wherein the resin comprises at least one compound selected from the group consisting of an ethylene-vinyl acetate (EVA) copolymer, an ethylene-acrylate copolymer, an ethylene-ethyl acrylate copolymer, an ethylene-n-butyl acrylate copolymer, and blends thereof.
12. The composition of claim 5 wherein the composition is capable of acting as an adhesive that adheres one layer of a multilayered structure to a second layer of the multilayered structure.
13. The composition of claim 12 wherein the multilayered structure comprises one or more polyethylene layers and one or more barrier layers.
14. The composition of claim 13 wherein the multilayered structure exhibits higher adhesion and higher clarity when compared to a film or sheet comprising, as a tie-layer adhesive, an unreacted blend of a grafted polyolefin and an olefin elastomer.
15. A process for making a graft composition, comprising:
(a) heating a polyolefin and an unsaturated monomer, optionally in the presence of a free-radical initiator, under conditions effective to produce a live, grafted polyolefin, and
(b) further reacting the live, grafted polyolefin and any residual polyolefin and/or unsaturated monomer with an olefin elastomer.
16. The process of claim 15 wherein after step (b) at least 90% of the unsaturated monomer is incorporated into the composition.
17. The process of claim 16 wherein after step (b) at least 98% of the unsaturated monomer is incorporated into the composition.
18. The process of claim 15 wherein the polyolefin is HDPE, the unsaturated monomer is maleic anhydride, and the olefin elastomer is EPR or EPDM.
19. The process of claim 15 which is integrated with a polyethylene production process such that polyethylene powder is blended in line with the graft composition to generate a mixture that is useful as a masterbatch or as a tie-layer adhesive.
20. The process of claim 19 wherein the polyethylene is LLDPE, the grafted polyolefin is maleic anhydride-grafted polyethylene, and the olefin elastomer is EPR or EPDM.