Positive electrode of lithium secondary battery and method for producing the same

1. A lithium secondary battery comprising a positive electrode for lithium secondary batteries, being a positive electrode used in lithium secondary batteries, comprising:

a positive electrode collector;

a barrier layer on the positive electrode collector, and comprising a composition having a conductive material, and at least one type of water-insoluble polymer that is soluble in organic solvents but insoluble in water, as a first binder wherein a content of the water-insoluble polymer in the barrier layer is 55 to 85 mass % with respect to 100 mass % of a total amount of the conductive material plus the water-insoluble polymer, and wherein the barrier layer is formed by heating the collector having the composition thereon up to 140 to 150° C.; and

a positive electrode active material layer, being stacked on the barrier layer, and having a positive electrode active material, and at least one type of aqueous polymer that is insoluble in organic solvents but soluble or dispersible In water, as a second binder;

a thickness of the barrier layer is 1 μm to 2 μm,

a thickness of the positive electrode active material layer is 30 μm to 80 μm, and

both an initial internal resistance value and an internal resistance after 500 cycles of charge-discharge under an environment temperature of 60° C. are lower than 40 mΩ.

2. The lithium secondary battery according to claim 1 , wherein the positive electrode active material is a lithium-transition metal complex oxide.

3. The lithium secondary battery according to claim 1 , wherein a thickness of the positive electrode active material layer is 15 to 80 times greater than the thickness of the barrier layer.

4. A method for manufacturing a lithium secondary battery having both an initial internal resistance value and an internal resistance after 500 cycles of charge-discharge under an environment temperature of 60° C. being lower than 40 mΩ, comprising the steps of:

preparing a composition for forming a barrier layer, having a conductive material, an organic solvent and at least one type of water-insoluble polymer that is soluble in organic solvents but insoluble in water, as a first binder, a content of the water-insoluble polymer in the composition being set to 55 to 85 mass % with respect to 100 mass % of a total amount of the conductive material plus the water-insoluble polymer;

applying the prepared composition onto a surface of a positive electrode collector such that the prepared composition has a thickness of 1 μm to 3 μm, and heating thereafter the collector up to 140 to 150° C., to form a barrier layer having a thickness of 1 μm to 2 μm on the positive electrode collector;

applying a composition for forming an active material layer, comprising a positive electrode active material, an aqueous solvent and at least one type of aqueous polymer that is insoluble in organic solvents but soluble or dispersible in water, as a second binder, onto a surface of the barrier layer, to form a positive electrode active material layer having a thickness of 30 μm to 80 μm on the barrier layer; and

assembling a lithium secondary battery using the positive electrode having the barrier layer and the positive active material layer.

5. The manufacturing method according to claim 4 , wherein a lithium-transition metal complex oxide is used as the positive electrode active material.

6. The manufacturing method according to claim 4 , wherein after application of the composition for forming an active material layer onto a surface of the barrier layer, the applied composition for forming an active material layer is dried at a temperature not higher than 150° C.