Phosphor with Ce
View Patent ↗The present disclosure provides an illuminating system including a light emitting device and a luminescent material disposed approximate the light-emitting device. The luminescent material includes a strontium silicon nitride (SrSi 6 N 8 ) doped by one of cerium (Ce 3+ ) and cerium (Ce 3+ ) and lithium (Li + ).
1. A method, comprising:
mixing stoichiometrically powdered strontium nitride (Sr 3 N 2 ), silicon nitride (Si 3 N 4 ), and cerium oxide (CeO 2 ) and lithium nitride (Li 3 N), thereby forming a mixture; and
sintering the mixture under a high pressure and a high temperature, thereby forming a luminescent material having a cerium (Ce 3+ ) and lithium (Li + ) co-doped strontium silicon nitride (SrSi 6 N 8 ).
2. The method of claim 1 , wherein the high pressure is equal to or greater than about 0.9 MPa under a nitrogen atmosphere.
3. The method of claim 1 , wherein the high temperature ranges between about 1800° C. and about 2000° C., and the sintering includes a sintering duration greater than about 0.5 hour.
4. The method of claim 1 , wherein the mixing stoichiometrically powdered strontium nitride (Sr 3 N 2 ), silicon nitride (Si 3 N 4 ), cerium oxide (CeO 2 ), and lithium nitride (Li 3 N) includes mixing powdered strontium nitride (Sr 3 N 2 ), silicon nitride (Si 3 N 4 ), cerium oxide (CeO 2 ), and lithium nitride (Li 3 N) with weights by percentage of about 25.16 to about 20.47, about 74.29 to about 74.06, about 0.46 to about 4.55, and about 0.09to about 0.92, respectively.
5. An illuminating system comprising:
a light emitting device; and
a luminescent material disposed approximate the light-emitting device, wherein the luminescent material includes a cerium (Ce 3+ ) and lithium (Li 30 ) co-doped strontium silicon nitride (SrSi 6 N 8 ).
6. The illuminating system of claim 5 , wherein the strontium silicon nitride is activated by cerium and lithium, formulated as Sr 1-2x Si 6 N 8 : Ce 3+ x , Li 3+ x .
7. The illuminating system of claim 6 , wherein x ranges between about 0.01 and about 0.5.
8. The illuminating system of claim 5 , wherein the luminescent material emits blue light excited by ultraviolet (UV) light and emits red light excited by blue light.
9. The illuminating system of claim 5 , wherein the luminescent material has an excitation spectrum with a peak ranging from 430 am to 490 nm.
10. The illuminating system of claim 5 , wherein the luminescent material is embedded in epoxy around the LED.
11. The illuminating system of claim 10 , wherein the luminescent material is powered and dispersed in the epoxy.
12. The illuminating system of claim 5 , wherein the light-emitting device includes an emission spectrum with a peak ranging from 430 nm to 490 nm.
13. The illuminating system of claim 5 , wherein the light-emitting device includes an indium gallium nitride (InGaN) LED.
14. A luminescent material comprising:
a rare earth element co-doped nitridosilicate phosphor formulated as M x-z Si y N 2/3×+11/9y :RE z ;
where M is one of calcium (Ca), strontium (Sr), and barium (Ba);
x, y, and z satisfy 0 <z <x <y; and
RE is a dopant having cerium (Ce 3+ ) and lithium (Li + ).
15. The luminescent material of claim 14 , wherein the rare earth element doped nitridosilicate phosphor includes:
a strontium silicon nitride (SrSi 6 N 8 ) doped by a dopant having cerium and lithium (Ce 3+ , Li + ) formulated as Sr 1-2x Si 6 N 8 : Ce 3+ x , Li 3+ x , wherein x ranges between about 0.01 and about 0.1.
16. The luminescent material of claim 14 , comprising an excitation spectrum peak ranging from 430 nm to 490 nm.
17. The luminescent material of claim 14 , comprising an excitation spectrum peak ranging from 300 nm to 420 nm.