High temperature high frequency magnet wire and method of making
A composite magnet wire includes, in an exemplary embodiment, a metal wire and a coating applied to an outer surface of the wire. The coating includes a polyimide polymer and a plurality of alumina nano particles dispersed in the polyimide polymer. The alumina nano particles have a surface treatment applied to outer surfaces of the alumina nano particles, where the surface treatment includes a phenyl-silane. The composite magnet wire has a thermal degradation temperature index of at least 300° C. as calculated in accordance with ASTM E1641 or D2307.
1. A composite magnet wire comprising:
a metal wire; and
a coating applied to an outer surface of said wire, said coating comprising a polyimide polymer comprising poly(biphenyltetracarboxylic dianhydride-co-phenylenediamine) and a plurality of alumina nano particles dispersed in said polyimide polymer, said alumina nano particles having a surface treatment applied to outer surfaces of said alumina nano particles, said surface treatment comprises a phenyl-silane;
said composite magnet wire having a thermal degradation temperature index of at least 300° C. as calculated in accordance with ASTM E1641 or ASTM D2307 (2005), wherein said coating comprises about 1% to about 6% by weight of said surface treated alumina nano particles, said coating on said outer surface has a thickness of about 25 μm to about 50 μm, and said alumina nano particles having an average particle size less than about 100 nanometers (nm).
2. The composite magnet wire in accordance with claim 1 , wherein said metal wire comprising at least one of copper or a copper alloy.
3. The composite magnet wire in accordance with claim 1 , wherein said alumina nano particles having an average particle size of about 20 nm to about 50 nm.
4. The composite magnet wire in accordance with claim 1 , wherein the metal wire comprises at least one of a silver plated copper wire, a nickel plated copper wire, a nickel cladded copper wire, an aluminum wire, or a copper cladded aluminum wire.
5. The composite magnet wire in accordance with claim 1 , wherein the phenyl-silane comprises at least one of trimethoxyphenylsilane, triethoxyphenylsilane, or mixtures thereof.
6. A composite magnet wire, comprising:
a metal wire, wherein the metal wire is at least one of copper, a copper alloy, silver plated copper, nickel plated copper, nickel cladded copper, aluminum, or copper clad aluminum; and
a coating applied to an outer surface of said wire, said coating comprising a polyimide polymer and a plurality of alumina nano particles dispersed in said polyimide polymer, said alumina nano particles having a surface treatment applied to outer surfaces of said alumina nano particles, said surface treatment comprises a phenyl-silane;
wherein
the polyimide polymer comprises poly(biphenyltetracarboxylic dianhydride-co-phenylenediamine);
the phenyl-silane comprises at least one of trimethoxyphenylsilane, triethoxyphenylsilane, or mixtures thereof;
the coating comprises about 1% to about 10% by weight of the surface treated alumina nano particles;
the coating on said outer surface has a thickness of about 25 μm to about 50 μm; and
the alumina nano particles having an average particle size of about 20 nm to about 50 nm;
said composite magnet wire having a thermal degradation temperature index of at least 300° C. as calculated in accordance with ASTM E1641 or ASTM D2307 (2005).