Scratch-resistant, impact-resistant polycarbonate moulding compositions having good mechanical properties II

1. A composition comprising

A) from 10 to 90 parts by weight aromatic polycarbonate and/or aromatic polyester carbonate,

B) from 0.5 to 30 parts by weight rubber-modified graft polymer,

C) from 0 to 40 parts by weight vinyl (co)polymer (C.1) and/or polyalkylene terephthalate (C.2),

D) from 0.1 to 10.0 parts by weight polyorganosiloxane/filler composition comprising

(D.1) at least one polyorganosiloxane comprising units of formula (IV):

R r SiO (4-r)/2   (IV)

wherein R is selected from the group consisting of vinyl, allyl, methallyl, 1-propenyl, 1-butenyl, 1-pentenyl, 5-hexenyl, butadienyl, hexadienyl, cyclopentenyl, cyclopentadienyl, cyclohexenyl, ethynyl, propargyl, 1-propynyl, methyl, 3-chloropropyl, 3,3,3-trifluoropropyl, perfluorohexylethyl, p-chlorophenyl and p-chlorobenzyl radicals,

r is 0, 1, 2 or 3,and

the average numerical value of r is from 1.9 to 2.1,

(D.2) from 1 to 200 parts by weight, based on 100 parts by weight of the polyorganosiloxane (D.1), of a filler selected from the group consisting of pyrogenic and precipitated silicas having BET surface areas of at least 50 m 2 /g (according to DIN 66131/2), and

(D.3) from 0 to 20 parts by weight, based on 100 parts by weight of the polyorganosiloxane (D.1), of at least one additive for preparing a granulate, and

(D.4) optionally at least one further auxiliary substance selected from the group consisting of processing aids, plasticisers, pigments and stabilisers,

E) from 0 to 20.0 parts by weight of an inorganic compound having a Mohs hardness of at least 2.5,

F) from 0 to 20 parts by weight of at least one phosphorus-containing flameproofing agent,

G) from 0 to 10 parts by weight of at least one further additive,

all parts by weight being normalised such that the sum of the parts by weight of all the components A+B+C+D+E+F+G in the composition is 100, and

wherein there is an increase in stress cracking resistance of at least 59.4% in engine oil, or an increase in stress cracking resistance of at least 20.4% in rape oil, or an increase in stress cracking resistance of at least 5.1% in hand lotion, over a control composition without component D), or

wherein the impact resistance of the composition is at least 208 kJ/m 2 .

2. A composition according to claim 1 , wherein component A is a mixture of a linear polycarbonate Al comprising bisphenol A having a weight-average molecular weight M w of 27,500 g/mol and a linear polycarbonate A2 comprising bisphenol A having a weight-average molecular weight M w of 19,500 g/mol.

3. A composition according to claim 1 , wherein the polyorganosiloxane of component D has a mean molecular weight M n of from 200,000 g/mol to 800,000 g/mol.

4. A composition according to claim 1 , wherein the graft base of component B has a mean particle size (d 50 value) of from 0.05 to 10.00 μm.

5. A composition according to claim 1 , wherein the graft base of component B is selected from the group consisting of diene rubbers, EP(D)M rubbers, acrylate, polyurethane, silicone, chloroprene and ethylene/vinyl acetate rubbers.

6. A composition according to claim 1 , wherein the graft polymer (B) comprises

B.1) 43 wt.% of an emulsion polymer of 27 wt.% acrylonitrile and 73 wt.% styrene on

B.2) 57 wt.% of a particulate crosslinked polybutadiene rubber having a mean particle diameter d 50 of 0.35 μm.

7. A composition according to claim 1 , wherein the phosphorus-containing flameproofing agent (F) is present and comprises a flameproofing agent of formula (V)

wherein

R 1 , R 2 , R 3 and R 4 , independently of one another, represent in each case optionally halogenated C 1 - to C 8 -alkyl, or C 5 - to C 6 -cycloalkyl, C 6 - to C 20 -aryl or C 7 - to C 12 -aralkyl, in each case optionally substituted by alkyl, and/or halogen each of the substituents n independently of the others represents 0 or 1,

q represents from 0.80 to 5.00 and

X represents a mono- or poly-nuclear aromatic radical having from 6 to 30 carbon atoms, or a linear or branched aliphatic radical having from 2 to 30 carbon atoms which can be OH-substituted and can contain up to 8 ether bonds.

8. A composition according to claim 1 , wherein component G is present and comprises at least one additive selected from the group consisting of flameproofing synergists, antidripping agents, lubricants and mould-release agents, nucleating agents, stabilizers, antistatics, colorings, pigments, and fillers and reinforcing agents.

9. A composition according to claim 1 adapted in the production of injection-molded and/or thermoformed molded articles.

10. A composition according to claim 1 , comprising

A) from 50-85 parts by wt. of aromatic polycarbonate and/or aromatic polyester carbonate,

B) from 1.0-25.0 parts by wt. of rubber-modified graft polymer,

C) from 1.0-30.0 parts by wt. of vinyl (co)polymer (C.1) and/or polyalkylene terephthalate (C.2),

D) from 0.3 to 8.0 parts by wt. polyorganosiloxane/filler composition,

E) from 1.0 to 15.0 parts by weight of an inorganic compound having a Mohs hardness of at least 2.5,

F) from 1.0-18.0 parts by wt. of at least one phosphorus-containing flameproofing agent,

G) from 0.5-8.0 parts by wt. of at least one further additive,

wherein all the parts by weight stated are standardized such that the sum of the parts by weight of all the components A+B+C+D+E+F+G in the composition is 100.

11. A composition according to claim 1 , comprising

A) from 60-75 parts by wt. of aromatic polycarbonate and/or aromatic polyester carbonate,

B) from 4.0-9.0 parts by wt. of rubber-modified graft polymer,

C) from 1.5-10 parts by wt. of vinyl (co)polymer (C.1) and/or polyalkylene terephthalate (C.2),

D) from 2.0 to 5.0 parts by weight polyorganosiloxane/filler composition,

E) from 3.0 to 12.0 parts by wt. of an inorganic compound having a mohs hardness of at least 2.5,

F) from 3.0-15.0 parts by wt. of at least one phosphorus-containing flameproofing agent,

G) from 1.0-6.0 parts by wt. of at least one further additive,

wherein all the parts by weight stated are standardized such that the sum of the parts by weight of all the components A+B+C+D+E+F+G in the composition is 100.

12. A composition according to claim 1 , wherein the inorganic compound of component E is present and is selected from the group consisting of silicates, aluminosilicates, carbides, nitrides and metal oxides.

13. A composition according to claim 12 , wherein the metal oxides are selected from the group consisting of boron nitride, silicon carbide, tungsten carbide, boron carbide, cerium oxide, kaolin and aluminium oxide (corundum).

14. A composition according to claim 1 , wherein component E is present and comprises hollow ceramic spheres having an Al 2 O 3 content of from 5 to 25 wt. %.

15. A composition according to claim 14 , wherein the hollow ceramic spheres have a compressive strength of from 50 to 700 MPa.

16. A composition according to claim 1 , wherein component B is at least one graft polymer of

B.1 5 to 95 wt. % of at least one vinyl monomer on

B.2 95 to 5 wt. % of at least one graft base having glass transition temperature of <10° C., selected from the group consisting of diene rubbers, EP(D)M rubbers, acrylate, polyurethane, silicone, chloroprene, and ethylene/vinyl acetate rubbers.

17. A composition according to claim 16 , wherein component B.1 is mixture of B.1.1 50 to 99 parts by wt. of at least one monomer selected from the group consisting of styrene, a-methylstyrene, p-methylstyrene, p-chlorostyrene, methyl methacrylate, and ethyl methacrylate, and B.1.2 1 to 50 parts by wt. of at least one monomer selected from the group consisting of acrylonitrile, methacrylnitrile, methyl methacrylate, n-butyl acrylate, tert-butyl acrylate, and maleic anhydride.