Ceramic proppants
A sintered, generally spherical ceramic body, having an alumina content of from about 52 to about 58 weight percent distributed substantially homogeneously throughout the body, a silica content from about 32 to about 39 weight percent distributed substantially homogeneously throughout the body, an apparent specific gravity of about 2.63 to about 2.67, and a bulk density of about 1.48 to about 1.56 grams per cubic centimeter.
1. A sintered, generally spherical ceramic body, comprising:
an alumina content between about 32 and about 39 weight percent distributed substantially homogeneously throughout the body;
a silica content between about 52 and about 58 weight percent distributed substantially homogeneously throughout the body;
an iron oxide content of about 3 weight percent;
a titania content of about 2 weight percent titania;
with the remainder being alkali and alkali earth metal oxides;
having an apparent specific gravity of about 2.65; and
having a bulk density of about 1.50 grams per cubic centimeter.
2. The sintered body of claim 1 wherein the body is characterized by a crush of less than about 10 percent at 7500 psi.
3. The sintered body of claim 1 wherein the body is characterized by a crush of less than about 5 percent at 7500 psi.
4. The sintered body of claim 1 wherein the body is characterized by a crush of less than about 10 percent at 8000 psi.
5. The sintered body of claim 1 wherein the alumina content is between about 35 and about 38 weight percent and the silica content is between about 54 and about 57 weight percent.
6. The sintered body of claim 1 wherein the sintered body has a Krumbein roundness value of at least 0.9.
7. A high strength ceramic body, comprising:
an alumina content between about 32 and about 39 weight percent distributed substantially homogeneously throughout the body; and
a silica content between about 52 and about 58 weight percent distributed substantially homogeneously throughout the body;
wherein the body has an apparent specific gravity of about 2.65;
wherein the body has a bulk density of about 1.50 grams per cubic centimeter;
wherein the body has an iron oxide content of about 3 weight percent;
wherienthe body has a titania content of about 2 weight percent;
wherein the remainder of the body is alkali and alkali earth metal oxides;
wherein the body has a specific gravity between 2.61 and 2.65 grams per cubic centimeter; and
wherein the body has an ambient temperature permeability of at least about 100,000 millidarcies at 8,000 psi.
8. The high strength ceramic body of claim 7 wherein the body has a silica content of between 54 and 57 weight percent.
9. The high strength ceramic body of claim 8 wherein the body contains about 36 weight percent alumina and about 56 weight percent silica.
10. The high strength ceramic body of claim 7 wherein the body has a Krumbein sphericity of at least 0.9.
11. The high strength ceramic body of claim 7 wherein the body further includes a crush strength enhancer selected from the group of rutile, bentonite, ball clay, fireclay, nepheline syenite, fused bauxite dust, wollastonite, feldspar and talc.