The present invention relates to a low-V 2 O 5 -content and even V 2 O 5 -free porcelain enamel with improved dish-washer resistance, very good acid resistance and good adherence on various substrates. The invention moreover relates to a transparent low-V 2 O 5 -content and even V 2 O 5 -free porcelain enamel frit for application of enamel coatings with infinite color range on a substrate made of aluminum, cast aluminum, aluminum alloy, aluminum-magnesium alloy, cast aluminum alloy, copper, austenitic stainless steel and mild steel, presenting improved dish-washer resistance, good acid resistance and good adherence on the substrate. The composition of the porcelain enamel in question comprises about 30 wt-% to about 50 wt-% SiO 2 , about 30 wt-% to about 40 wt-% R 2 O, about 15 wt-% to about 25 wt-% TiO 2 , about 0 wt-% to about 5 wt-% RO, about 0 wt-% to about 4 wt-% V 2 O 5 , about 0.3 wt-% to about 7 wt-% Fe 2 O 3 , about 0 wt-% to about 3 wt-% Sb 2 O 3 , about 0 wt-% to about 3 wt-% SnO 2 , about 0 wt-% to about 2 wt-% B 2 O 3 , about 0 wt-% to about 3 wt-% Al 2 O 3 , about 0 wt-% to about 4 wt-% P 2 O 5 , about 0 wt-% to about 1 wt-% MoO 3 , about 0 wt-% to about 2 wt-% F 2 , about 0 wt-% to about 4 wt-% ZrO 2 , about 0 wt-% to about 4 wt-% ZnO, about 0 wt-% to about 6 wt-% NO x , R 2 O is a combination of alkaline oxides selected from the group of: Na 2 O 10-23 mol %, K 2 O 7-20 mol % and Li 2 O 1-6.5 mol %, wherein RO represent at least one earth alkali oxide and wherein the molar ratio of (Li 2 O+B 2 O 3 ) to TiO 2 amounts to 0.2 to 0.6.
1. Transparent porcelain enamel compositions for enameling a substrate selected from the group of aluminium, cast aluminium, aluminium alloy, and aluminium-magnesium alloy, said composition including a glass frit, said glass frit based on 100 wt-% comprising each by weight:
about 30 wt-% to about 50 wt-% SiO 2 ,
about 30 wt-% to about 40 wt-% R 20 ,
about 15 wt-% to about 25 wt-% TiO 2 ,
about 0 wt-% to about 5 wt-% RO,
about 0 wt-% to about 4 wt-% V 2 O 5 ,
about 0.3 wt-% to about 5 wt-% Fe 2 O 3 ,
about 0 wt-% to about 5 wt-% Sb 2 O 3
about 0 wt-% to about 3 wt-% SnO 2
about 0 wt-% to about 2 wt-% B 2 O 3 ,
about 0 wt-% to about 3 wt-% Al 2 O 3 ,
about 0 wt-% to about 4 wt-% P 2 O 5 ,
about 0 wt-% to about 1 wt-% MoO 3 ,
about 0 wt-% to about 2 wt-% F 2 ,
about 0 wt-% to about 4 wt-% ZrO 2 ,
about 0 wt-% to about 4 wt-% ZnO and
about 0 wt-% to about 6 wt-% N 2 O 5
wherein
R 2 O is a combination of alkaline oxides selected from the group of Na 2 O, K 2 O, and Li 2 O, in molar fractions, based on the entirety of the glass composition, of:
Na 2 O 10-23 mol %
K 2 O 7-20 mol %
Li 2 O 1-6.5 mol %,
wherein the molar ratio of (Li 2 O+B 2 O 3 ) to TiO 2 amounts to 0.2 to 0.6, and
RO is an earth alkaline oxide selected from the group of CaO, SrO, BaO, MgO and combinations thereof.
2. The composition according to claim 1 being void of V 2 O 5 .
3. The compositions according to claim 1 further comprising inorganic pigments and/or effect pigments.
4. The composition of claim 1 further comprising mill additions selected from the group consisting of boric acid, formic acid, molybdic acid, sodium molybdate, ammonium molybdate, potassium silicate, sodium silicate, lithium silicate, hydroxides, fluorides, carbonates, nitrate, nitrite, aerosols, urea, inorganic pigments, effect pigments and combinations thereof.
5. Substrate selected from the group of aluminium, cast aluminium, aluminium alloy, aluminium-magnesium alloy, copper, austenitic stainless steel and mild steel having an enameled surface made of an enamel frit according to claim 1 .
6. A process of making a porcelain coated substrate, comprising:
a) applying a porcelain composition to a substrate of aluminium, cast aluminium, aluminium alloy, or aluminium-magnesium alloy, said composition comprising:
based on 100% by weight:
about 30 wt-% to about 50 wt-% SiO 2 ,
about 30 wt-% to about 40 wt-% R 2 O,
about 15 wt-% to about 25 wt-% TiO 2 ,
about 0 wt-% to about 5 wt-% RO,
about 0 wt-% to about 4 wt-% V 2 O 5 ,
about 0.3 wt-% to about 5 wt-% Fe 2 O 3 ,
about 0 wt-% to about 5 wt-% Sb 2 O,
about 0 wt-% to about 3 wt-% SnO 2
about 0 wt-% to about 2 wt-% B 2 O 3 ,
about 0 wt-% to about 3 wt-% Al 2 O 3 ,
about 0 wt-% to about 4 wt-% P 2 O 5 ,
about 0 wt-% to about 1 wt-% MoO 3 ,
about 0 wt-% to about 2 wt-% F 2 ,
about 0 wt-% to about 4 wt-% ZrO 2 ,
about 0 wt-% to about 4 wt-% ZnO and
about 0 wt-% to about 6 wt-% N 2 O 5
wherein
R 2 O is a combination of alkaline oxides selected from the group of Na 2 O, K 2 O, and Li 2 O, in molar fractions, based on the entirety of the glass composition, of:
Na 2 O 10-23 mol %
K 2 O 7-20 mol %
Li 2 O 1-6.5 mol %,
wherein the molar ratio of (Li 2 O+B 2 O 3 ) to TiO 2 amounts to 0.2 to 0.6, and
RO is an earth alkaline oxide selected from the group of CaO, SrO, BaO, MgO and combinations thereof; and
b) firing said porcelain composition applied to said substrate at a temperature between 520-580° C.