Glass substrate for information recording medium and information recording medium
A glass substrate for information recording medium, said glass substrate being composed of an aluminosilicate glass containing 60-75% by mass of SiO 2 , 5-18% by mass of Al 2 O 3 , 3-10% by mass of Li 2 O, 3-15% by mass of Na 2 O and 0.5-8% by mass of ZrO 2 relative to the entire glass components. The glass substrate for information recording medium contains neither As (arsenic) nor Sb (antimony), while containing at least one substance selected from the group consisting of SO 3 (sulfurous acid), F (fluorine), Cl (chlorine), Br (bromine) and I (iodine), as a refining agent. The molar ratio of the total amount of the refining agent to the amount of Al 2 O3 is within the range of 0.02-0.20.
1. A glass substrate for an information recording medium made of aluminosilicate glass containing 60% to 75% by mass of SiO 2 , 5% to 18% by mass of Al 2 O 3 , 3% to 10% by mass of Li 2 O, 3% to 15% by mass of Na 2 O, and 0.5% to 8% by mass of ZrO 2 with respect to whole glass components, and containing neither As (arsenic) element nor Sb (antimony) element, comprising:
a fining agent containing SO 3 (sulfurous acid), wherein a molar ratio of a whole amount of the fining agent to the Al 2 O 3 , which is (the whole amount of the fining agent)/Al 2 O 3 , is within a range of 0.02 to 0.20; and
wherein a total content of the fining agent is in a range of 1% by mass or less with respect to the whole glass components.
2. The glass substrate for an information recording medium of claim 1 , wherein the glass substrate for an information recording medium is chemically strengthened by ion exchange.
3. The glass substrate for an information recording medium of claim 1 , wherein the fining agent contains at least one type selected from the group consisting of F (fluorine), Br (bromine), and I (iodine).
4. The glass substrate for an information recording medium of claim 1 , wherein a molar ratio of a whole amount of the fining agent to the Al 2 O 3 is selected such that clarification reaction by a change in solubility is adequate to sufficiently remove gas bubbles within the glass substrate when it is in a molten state.
5. The glass substrate for an information recording medium of claim 1 , wherein a molar ratio of a whole amount of the fining agent to the Al 2 O 3 is selected such that clarification reaction by a valence change is adequate to sufficiently remove gas bubbles within the glass substrate when it is in a molten state.
6. An information recording medium, comprising:
a glass substrate for an information recording medium made of aluminosilicate glass containing 60% to 75% by mass of SiO 2 , 5% to 18% by mass of Al 2 O 3 , 3% to 10% by mass of Li 2 O, 3% to 15% by mass of Na 2 O, and 0.5% to 8% by mass of ZrO 2 with respect to whole glass components, and containing neither As (arsenic) element nor Sb (antimony) element, comprising:
a fining agent containing SO 3 (sulfurous acid), wherein a molar ratio of a whole amount of the fining agent to the Al 2 O 3 , which is (the whole amount of the fining agent)/Al 2 O 3 , is within a range of 0.02 to 0.20; and
wherein a total content of the fining agent is in a range of 1% by mass or less with respect to the whole glass components; and
a recording layer provided on the glass substrate.
7. The information recording medium of claim 6 , wherein the glass substrate is chemically strengthened by ion exchange.
8. The information recording medium of claim 6 , wherein the fining agent contains at least one type selected from the group consisting of F (fluorine), Br (bromine), and I (iodine).
9. The information recording medium of claim 6 , wherein a molar ratio of a whole amount of the fining agent to the Al 2 O 3 is selected such that clarification reaction by a change in solubility is adequate to sufficiently remove gas bubbles within the glass substrate when it is in a molten state.
10. The information recording medium of claim 6 , wherein a molar ratio of a whole amount of the fining agent to the Al 2 O 3 is selected such that clarification reaction by a valence change is adequate to sufficiently remove gas bubbles within the glass substrate when it is in a molten state.