Plastic formulation and method for the production of plastic bottles in a two-stage stretch blow-molding process
An exemplary plastic formulation is disclosed for the production of plastic bottles in a two-stage stretch blow-molding process, and includes at least 60% of HDPE (High Density Polyethylene) having a density of 0.941 g/cm 3 to 0.965 g/cm3 and according to ISO 1133 a melt index 190° C./2.16 kg of 0.1 to 0.9 g/10 min. The HDPE contains a mono-modal or multi-modal HDPE having a second melt index 190° C./21.6 kg of 5 g/10 min to 50 g/10 min according to ISO 1133. A method is disclosed for producing a plastic bottle in a two-stage stretch blow-molding process using the plastic formulation.
1. Plastic formulation for producing plastic bottles in a two-station stretch blow-molding process, from a plastic preform, produced from an injection molding process or a flow molding process, for a plastic bottle producible in a separate stretch blow-molding process, the preform being stretchable axially and radially, and the plastic formulation comprising:
at least 60% HDPE (high density polyethylene) of a density from 0.941 g/cm 3 to 0.965 g/cm 3 and with a first melt index 190° C./2.16 kg from 0.1 to 0.9 g/10 min according to ISO 1133, the HDPE comprising a monomodal or multimodal HDPE with a second melt index 190° C./21.6 kg from 5 g/10 min to 50 g/10 min according to ISO 1133, and wherein the plastic preform is heated to a temperature from 115° C. to 135° C. for processing in the stretch blow-molding process.
2. Plastic formulation as claimed in claim 1 , comprising:
0% to 40% calcium carbonate as a filler.
3. Plastic formulation as claimed in claim 1 , comprising:
a proportion of HDPE in the plastic formulation of at least 90%.
4. Plastic formulation as claimed in claim 3 , comprising:
0%-10% calcium carbonate and/or talc and/or a mixture of polymers which are suitable for a blow molding process as a filler.
5. Plastic formulation as claimed in claim 1 , comprising:
0% to 4% of a dye based on titanium oxide and/or zinc sulfide.
6. Plastic formulation as claimed in claim 1 , comprising:
HDPE with a first melt index of 190° C./2.16 kg of roughly 0.3 g/10 min and a second melt index of 190° C./21.6 kg of 30 g/10 min and a bimodal distribution.
7. Plastic formulation as claimed in claim 4 , comprising:
0% to 4% of a dye based on titanium oxide and/or zinc sulfide.
8. Plastic formulation as claimed in claim 7 , comprising:
HDPE with a first melt index of 190° C./2.16 kg of roughly 0.3 g/10 min and a second melt index of 190° C./21.6 kg of 30 g/10 min and a bimodal distribution.