Protective coatings for inorganic substrates and associated methods
A composition for protecting a surface of an inorganic substrate, such as concrete, terrazzo, or ceramic tile, includes a silicate (e.g., an alkali metal polysilicate or a colloidal silica), a siliconate (e.g., a metal siliconate, such as an alkali metal methyl siliconate, etc.), acrylic latex, a silane coupling agent, and a solvent, such as ethylene glycol monobutyl ether. Inorganic substrates, such as concrete, stone, and ceramic materials, with such a composition on their surfaces are also disclosed, as are methods for polishing and protecting inorganic substrates.
1. A composition for protecting surfaces of inorganic substrates, consisting essentially of:
a silicate;
a siliconate;
acrylic latex;
a silane coupling agent;
a solvent; and
water.
2. The composition of claim 1 , non-essentially including a leveling agent.
3. The composition of claim 2 , wherein the leveling agent comprises a surfactant.
4. The composition of claim 3 , wherein the surfactant comprises a fluorosurfactant.
5. The composition of claim 2 , wherein the leveling agent comprises a tris(2-butoxyethyl)phosphate having the chemical formula C 18 H 39 O 7 P.
6. The composition of claim 1 , wherein the siliconate includes at least one of potassium methyl siliconate and sodium methyl siliconate.
7. The composition of claim 1 , wherein the silane coupling agent comprises N-β(aminoethyl)-r-aminopropyl-trimethoxysilane.
8. The composition of claim 1 , wherein the silicate comprises lithium polysilicate.
9. The composition of claim 8 , wherein the solvent comprises at least one of ethylene glycol monobutyl ether, dipropylene glycol dimethyl ether and dipropylene glycol n-butyl ether.
10. The composition of claim 9 , wherein:
the lithium polysilicate makes up about 20% to about 50% of the weight of the composition;
the siliconate makes up about 2% to about 15% of the weight of the composition;
the acrylic latex makes up about 4% to about 50% of the weight of the composition;
the silane coupling agent makes up about 1% to about 10% of the weight of the composition; and
the ethylene glycol monobutyl ether makes up about 0.5% to about 2% of the weight of the composition.