Granted Patent B2

US 8,652,761 · App. 13/030,810 · Granted Feb 18, 2014

Abstract

Claims (41)

1. A method of thermally developing a photocurable printing blank to produce a relief pattern comprising a plurality of printing dots, wherein the photocurable printing blank comprises a backing layer having at least one photocurable layer disposed thereon and a laser ablatable mask layer disposed on top of the at least one photocurable layer, the method comprising the step of:

a) imaging the at least one photocurable layer by selectively ablating the laser ablatable mask layer to create an image on the surface of the at least one photocurable layer;

b) laminating an oxygen barrier membrane to a top of the laser ablated mask layer;

c) exposing the printing blank to actinic radiation through the oxygen barrier membrane and laser ablatable mask layer to one or more sources of actinic radiation to selectively crosslink and cure portions of the at least one photocurable layer, wherein the at least one photocurable layer is crosslinked and cured in the portions not covered by the mask layer, thereby creating the relief pattern;

d) removing the oxygen barrier membrane from the top of the laser ablated mask layer; and

e) thermally developing the photocurable printing blank to remove the laser ablated mask layer and uncured portions of the at least one photocurable layer and reveal the relief pattern.

2. The method according to claim 1 , wherein the printing dots have one or more characteristics selected from:

a) steep shoulder angles, wherein the shoulder angle of each of the printing dots is such that the overall shoulder angle is greater than about 50°;

b) planarity of the printing dot surface, wherein the planarity of a top surface of the printing dots is such that the radius of curvature of the top surface of the printing dots, r t , is greater than the total thickness of the at least one layer of photocurable material;

c) sufficient depth of relief between the printing dots, wherein relief between the printing dots is greater than about 9% of overall relief;

d) sharpness of the edge at the point where the printing dot top transitions to the printing dot shoulder, wherein a ratio of r e :p is less than 5%; and

e) low surface roughness, wherein the surface roughness of the top of the printing dots is less than about 700 nm.

3. The method according to claim 2 , wherein the at least one characteristic comprises steep shoulder angles, wherein the shoulder angle of each of the printing dots is such that the overall shoulder angle is greater than about 50°.

4. The method according to claim 3 , wherein the shoulder angle of each of the plurality of printing dots is such that overall shoulder angle is greater than about 70°.

5. The method according to claim 2 , wherein the at least one characteristic comprises planarity of the printing dot surface, wherein the planarity of a top surface of the printing dots is such that the radius of curvature of the top surface of the printing dots r + , is greater than the thickness of the at least one layer of photocurable material.

6. The method according to claim 2 , wherein the at least one characteristic comprises low surface roughness, wherein the surface roughness of the top of the printing dots is less than about 700 nm.

7. The method according to claim 6 , wherein the surface roughness of the top of the plurality of printing dots is less than about 800 nm.

8. The method according to claim 2 , wherein relief is greater than about 12% of the overall relief.

9. The method according to claim 2 , wherein the at least one characteristic comprises edge sharpness of the printing dots at the point where the printing dot top transitions to the printing dot shoulder, wherein a ratio of r e :p is less than 5%.

10. The method according to claim 9 , wherein the ratio of r e :p is less than 2%.

11. The method according to claim 1 , wherein the oxygen barrier membrane is selected from the group consisting of polyamides, polyvinyl alcohol, hydroxyalkyl cellulose, polyvinyl pyrrolidinone, copolymers of ethylene and vinyl acetate, amphoteric interpolymers, cellulose acetate butyrate, alkyl cellulose, butryal, cyclic rubbers, and combinations of one or more of the foregoing.

12. The method according to claim 1 , wherein the oxygen barrier membrane comprises a clear film selected from the group consisting of polypropylene, polyethylene, polyvinyl chloride, polyester and combinations of one or more of the foregoing.

13. The method according to claim 12 , wherein the oxygen barrier membrane comprises a polypropylene film or a polyethylene terephthalate film.

14. The method according to claim 1 , wherein the oxygen barrier membrane has a thickness of between about 1 and 100 microns.

15. The method according to claim 14 , wherein the oxygen barrier membrane has a thickness of between about 1 and about 20 microns.

16. The method according to claim 1 , wherein the oxygen barrier membrane has an optical transparency of at least about 50%.

17. The method according to claim 16 , wherein the oxygen barrier membrane has an optical transparency of at least about 75%.

18. The method according to claim 1 , wherein the oxygen barrier membrane has an oxygen diffusion coefficient of less than 6.9×10 −9 m 2 /sec.

19. The method according to claim 18 , wherein the oxygen barrier membrane has an oxygen diffusion coefficient of less than 6.9×10 −10 m 2 /sec.

20. The method according to claim 19 , wherein the oxygen barrier membrane has an oxygen diffusion coefficient of less than 6.9×10 −11 m 2 /sec.

21. The method according to claim 1 , wherein the step of thermally developing the printing blank comprises:

a) softening non-crosslinked polymer on the imaged and exposed surface of the printing blank by contacting the imaged and exposed surface with an absorbent layer capable of absorbing non-crosslinked portions of the at least one layer of photocurable material when it has been heated to a temperature of between 40° and 200° C.,

b) heating said at least one layer of photocurable material to a temperature of between 40° and 200° C. and allowing the non-crosslinked portions of the at least one layer of photocurable material in contact with the absorbent layer to be absorbed by said absorbent layer, and

c) removing said absorbent layer containing the non-crosslinked portion of the at least one photocurable layer, whereby the relief pattern is revealed.

22. The method according to claim 1 , wherein the printing blank is not imaged in an inert environment.

23. The method according to claim 1 , wherein the printing dots have one or more characteristics selected from:

a) steep shoulder angles, wherein the shoulder angle of each of the printing dots is such that the overall shoulder angle is greater than about 50° C.;

b) planarity of the printing dot surface, wherein the planarity of a top surface of the printing dots is such that the radius of curvature of the top surface of the printing dots, r t , is greater than the total thickness of the at least one layer of photocurable material;

c) sufficient depth of relief between the printing dots, wherein relief between the printing dots is greater than about 9% of the overall relief;

d) sharpness of the edge at the point where the printing dot top transitions to the printing dot shoulder, wherein a ratio of r e :p is less than 5%; and

e) low surface roughness, wherein the surface roughness of the top of the printing dots is less than about 800 nm.