Bio-based adhesive material
An adhesive product and method of making the product replaces asphalt in the manufacture of roofing shingles and pavement. The method comprises steps of forming a mixture of oil comprising fatty acids and a powdered material; maintaining the oil to powdered material weight ratio in the mixture between 1 to 0.01 and 1 to 4.9; heating the mixture to a reaction temperature greater than 100 degrees Centigrade; maintaining the reaction temperature for at least five minutes; and, injecting air into the mixture while maintaining the reaction temperature. In making a roofing shingle, the method includes additional steps of: applying the heated mixture to a fiberglass mat sheet from an upstream roll to form a tacky coated strip; and, adding a layer of granules to the tacky coated strip. The adhesive material of this method comprises polymerized oil and the powdered material.
1 . A method of making an adhesive material to replace asphalt in the manufacture of roof shingles or pavement, the method comprising the steps of:
forming a mixture by combining:
oil comprising fatty acids; and
a powdered material operable to facilitate the polymerization of the oil;
maintaining the oil to powdered material weight ratio in the mixture between 1 to 0.01 and 1 to 4.9;
heating the mixture to a reaction temperature greater than 100 degrees Centigrade;
maintaining the reaction temperature for a period of time longer than about five minutes; and
injecting air into the mixture while maintaining the reaction temperature.
2 . The method of claim 1 , further comprising the step of obtaining waste cooking oil for use as the oil in the mixture.
3 . The method of claim 1 , further comprising the step of selecting the powdered material from the group consisting of: fly ash; sand; cement; limestone; clay; talc; mica; alumina oxide; dolomite; gypsum; and mixtures thereof.
4 . The method of claim 1 , further comprising the step of obtaining the oil from a source selected from the group consisting of: a vegetable; a plant; an alga; an animal fat; and mixtures thereof.
5 . The method of claim 1 , wherein the reaction temperature is within a range of between about 130 degrees Centigrade and about 230 degrees Centigrade.
6 . The method of claim 1 , wherein the period of time for maintaining the reaction temperature comprises about 0.5 hours to about 5 hours.
7 . The method of claim 1 , further comprising the step of maintaining the oil to powdered material weight ratio between 1 to 0.5 and 1 to 3.
8 . The method of claim 1 , further comprising the steps of:
uniformly distributing the air in the mixture; and
maintaining an air to oil ratio in the mixture within a range of 0.02 to 2.0 liters air per gram of oil.
9 . The method of claim 1 , further comprising the steps of:
applying the heated mixture to a fiberglass mat sheet from an upstream roll to form a tacky coated strip; and
adding a layer of granules to the tacky coated strip.
10 . The method of claim 1 , further comprising the step of stirring the mixture while maintaining the reaction temperature.
11 . The method of claim 1 , wherein the step of injecting air into the mixture is performed by bubbling air into the mixture.
12 . The method of claim 1 , wherein the step of injecting air into the mixture is performed by rotating the mixture in a rotary drum.
13 . The adhesive material derived from the method of claim 1 comprising:
polymerized oil; and
the powdered material.