Electrode composite material of lithium ion battery, method for making the same, and lithium ion battery using the same
View Patent ↗An electrode composite material includes an individual electrode active material particle and a protective film coated on a surface of the particle. A composition of the protective film is at least one of Al x M y PO 4 and Al x M y (PO 3 ) 3 , M represents at least one chemical element selected from the group consisting of Cr, Zn, Mg, Zr, Mo, V, Nb, and Ta, and a valence of M is represented by k, wherein 0<x<1, 0<y<1, and 3x+ky=3.
1. A method for making an electrode composite material, the method comprising steps of:
providing a modifier and a plurality of electrode active material particles, the modifier being a first mixture of a phosphorous source having a phosphate radical, a trivalent aluminum source, and a metallic oxide provided in a liquid phase solvent;
mixing the plurality of electrode active material particles and the modifier to form a second mixture, and
drying and heat treating the second mixture to form the electrode composite material.
2. The method of claim 1 , wherein the phosphorous source comprises a material selected from the group consisting of phosphoric acid, triammonium phosphate, aluminum phosphate, ammonium dihydrogen phosphate, aluminum dihydrogen phosphate, diammonium hydrogen phosphate, dialuminum hydrogen phosphate, and combinations thereof.
3. The method of claim 1 , wherein the trivalent aluminum source comprises a material selected from the group consisting of aluminum hydroxide, aluminum oxide, aluminum phosphate, aluminum dihydrogen phosphate, dialuminum hydrogen phosphate, and combinations thereof.
4. The method of claim 1 , wherein the metallic oxide comprises a material selected from the group consisting of chromium trioxide, zinc oxide, copper oxide, magnesium oxide, zirconium dioxide, molybdenum trioxide, vanadium pentoxide, niobium pentoxide, tantalum pentoxide, and combinations thereof.
5. The method of claim 1 , wherein the phosphorous source and the trivalent aluminum source both comprise a material selected from the group consisting of aluminum phosphate, aluminum dihydrogen phosphate, dialuminum hydrogen phosphate, and combinations thereof.
6. The method of claim 1 , wherein the liquid phase solvent comprises a material selected from the group consisting of water, N-methyl-pyrrolidone, and combinations thereof.
7. The method of claim 1 , wherein a molar ratio of the trivalent aluminum source, the metallic oxide, and the phosphorous source is set by (Mol Al +Mol Metal ):Mol p =about 1:2.5 to about 1:4, Mol Al is the amount of substance of the aluminum element in the trivalent aluminum source, Mol Metal is the amount of substance of the metallic element in the metallic oxide, and Mol p is the amount of substance of the phosphorous element in the phosphorous source.
8. The method of claim 1 , wherein a total mass of the phosphate radical in the phosphorous source, the aluminum element in the trivalent aluminum source, and the metallic element in the metallic oxide, divided by a volume of the modifier is in a range from about 0.02 g/ml to about 0.08 g/ml.
9. The method of claim 1 , wherein the phosphorous source is phosphoric acid, the trivalent aluminum source is aluminum hydroxide, and the metallic oxide is chromium trioxide.
10. The method of claim 1 , wherein a temperature of the heat treating is in a range from about 300° C. to about 800° C.
11. The method of claim 1 , wherein the modifier is a clear solution fabricated by the following steps:
providing a solution of the phosphorous source having the phosphate radical;
putting the trivalent aluminum source into the solution of the phosphorous source having the phosphate radical to form a suspension; and
adding the metallic oxide to the suspension to react with the suspension to form the clear solution.
12. A method for making an electrode composite material, the method comprising steps of:
providing a modifier and a plurality of electrode active material particles, the modifier being a clear solution fabricated by the following substeps:
providing a solution of a phosphorous source having a phosphate radical;
putting a trivalent aluminum source into the solution of the phosphorous source having the phosphate radical to form a suspension; and
adding a metallic oxide to the suspension to react with the suspension to form the clear solution, wherein a molar ratio of the trivalent aluminum source, the metallic oxide and the phosphorous source is set by (Mol Al +Mol Metal ):Mol p =about 1:2.5 to about 1:4, Mol Al is the amount of substance of an aluminum element in the trivalent aluminum source, Mol Metal is the amount of substance of an metallic element in the metallic oxide, and Mol p is the amount of substance of an phosphorous element in the phosphorous source;
mixing the plurality of electrode active material particles and the modifier to form a mixture; and
drying and heat treating the mixture to form the electrode composite material.