Impact-resistant modified polyamide moulding compound and container formed therefrom
Disclosed is an impact-resistant modified polyamide molding compound which is suitable in particular for the production of containers having a good oxygen barrier and low-temperature impact strength. Also disclosed are containers which are produced from the thermoplastic polyamide molding compound. In particular, storage or transport containers for industrial chemicals, agrochemicals, the cosmetic industry, pharmaceutical industry or foodstuffs industry can be produced from the polyamide molding compound of the invention.
1. A thermoplastic polyamide moulding compound, comprising
a) 71 to 89% by weight of a copolyamide MXD6/MXDI, the molar proportion of isophthalic acid, relative to the total quantity of the diacids, isophthalic acid and adipic acid, being 1 to 30% by mol,
b) 11-29% by weight of at least one acid-modified copolyolefin elastomer or at least one acid-modified blend of a plurality of copolyolefin elastomers, comprising the following monomeric units in the following molar proportions:
i) 65-90% by mol ethylene
ii) 8-33% by mol propylene
iii) 2-25% by mol but-1-ene, and
c) 0 to 8% by weight of additives,
components a) to c) adding up to 100% by weight.
2. The moulding compound according to claim 1 , wherein the molar proportion of isophthalic acid in the copolyamide MXD6/MXDI, relative to the total quantity of the diacids, isophthalic acid and adipic acid, is 1 to 20% by mol.
3. The moulding compound according to claim 1 , wherein the copolyamide MXD6/MXDI has at most 70 meq/kg amino end groups.
4. The moulding compound according to claim 1 , wherein the modification degree of the acid-modified copolyolefin elastomer or of the at least one acid-modified blend of a plurality of copolyolefin elastomers is 0.3 to 1.5% by weight, relative to the acid-modified copolyolefin elastomer or the acid-modified blend of a plurality of copolyolefin elastomers.
5. The moulding compound according to claim 1 , wherein the acid modification of the copolyolefin elastomer or of the blend of a plurality of copolyolefin elastomers is effected by grafting with unsaturated carboxylic acids and/or unsaturated carboxylic acid derivatives.
6. The moulding compound according to claim 1 , wherein the relative viscosity of the polyamide MXD6/MXDI, measured in 0.5% by weight of m-cresol solution at 20° C., is 1.40 to 1.80.
7. The moulding compound according to claim 1 , wherein
a) the weight proportion of the copolyamide is 73 to 87% by weight, and
b) the weight proportion of the at least one acid-modified copolyolefin elastomer or of the at least one acid-modified blend of a plurality of copolyolefin elastomers is 13 to 27% by weight, relative to the moulding compound.
8. The moulding compound according to claim 1 , wherein, in addition to the copolymers a) and b), no further polymers and/or copolymers are contained and the moulding compound hence consists of components a) to c).
9. A multilayer container comprising at least one layer which is produced from a moulding compound according to claim 1 .
10. The container according to claim 9 , wherein at least the innermost layer is produced from the moulding compound.
11. The container according to claim 9 , wherein the at least one layer which is produced from the moulding compound has a layer thickness of 15 to 800 μm.
12. The container according to claim 9 , wherein the totality of the layers has a total layer thickness of 500 μm to 10 mm.
13. The container according to claim 9 , which, when filled with an ethylene glycol-water mixture in the volume ratio of 1:2 and after storage at −20° C. for 24 to 48 hours, and dropped from 1.8 m, does not break.
14. A method for storing agrochemicals, industrial chemicals, industrial precursor and intermediate products, cosmetic precursor products or products, pharmaceutical precursor products or products and/or precursor products for the foodstuffs industry comprising utilizing the container according to claim 9 .
15. The moulding compound of claim 2 , wherein the molar proportion of isophthalic acid in the copolyamide MXD6/MXDI, relative to the total quantity of the diacids, isophthalic acid and adipic acid, is 1 to 15% by mol.
16. The moulding compound according to claim 3 , wherein the copolyamide MXD6/MXDI has at most 5 to 50 meq/kg amino end groups.
17. The moulding compound according to claim 4 , wherein the modification degree of the acid-modified copolyolefin elastomer or of the at least one acid-modified blend of a plurality of copolyolefin elastomers is 0.4 to 1.2% by weight.
18. The moulding compound according to claim 5 , wherein the carboxylic acid derivative is selected from the group consisting of unsaturated carboxylic acid esters and unsaturated carboxylic acid anhydrides.