PET FOAM ARTICLES AND RELATED METHODS
PET foam articles and methods of forming the same are described herein. Processing conditions may be controlled to form PET foam sheets having desirable characteristics.
1 . A method of processing PET foam sheet comprising:
conveying a stream of PET polymeric material and blowing agent in an extruder, wherein the blowing agent is a mixture comprising carbon dioxide and nitrogen, wherein the ratio of carbon dioxide to nitrogen is between 4:1 and 1:1;
extruding the stream; and
forming a PET polymeric foam sheet.
2 . The method of claim 1 , further comprising introducing the blowing agent mixture into the polymeric material in the extruder through a port to form the stream of polymeric material and blowing agent.
3 . The method of claim 1 , wherein the blowing agent is present in an amount less than about 2.0% by weight of polymeric stream and blowing agent.
4 . The method of claim 1 , wherein the carbon dioxide is present in an amount less than about 2.0% by weight of polymeric stream and blowing agent.
5 . The method of claim 1 , wherein the nitrogen is present in an amount less than about 1.0% by weight of polymeric stream and blowing agent.
6 . The method of claim 1 , wherein the ratio of carbon dioxide to nitrogen is between 3:1 and 1:1
7 . The method of claim 1 , further comprising forming a single-phase solution from the stream of polymeric material and blowing agent in the extruder.
8 . The method of claim 7 , further comprising nucleating the single-phase solution by extruding the solution through the die.
9 . The method of claim 1 , wherein the die has a cross-sectional dimension that converges toward the die outlet.
10 . The method of claim 1 , wherein the PET foam sheet has an average cell size of less than 150 micron.
11 . The method of claim 1 , wherein the PET foam sheet has a density of less than 0.35 g/cm 3 .
12 . The method of claim 1 , wherein the PET foam sheet is substantially free of corrugation.
13 . The method of claim 1 , further comprising thermoforming the PET foam sheet to form a thermoformed PET foam article.
14 . A PET foam article comprising:
a PET foam having a density of less than 0.35 g/cm 3 , wherein the foam sheet has an average cell size of less than 150 microns and is substantially free of corrugation.
15 . The article of claim 14 , wherein the PET foam has a density of less than 0.30 g/cm 3 .
16 . The article of claim 14 , wherein the PET foam has an average cell size of less than 100 microns.
17 . The article of claim 14 , wherein the PET foam article is a sheet.
18 . The article of claim 14 , wherein the PET foam article is a thermoformed article.