Adhering systems

1. A system, relating to preventing delamination of a magnetizable laminate exposed to direct sunlight and relating to preventing fouling of cutting blades during cutting of said magnetizable laminate, said system comprising:

at least one flexible magnetizable laminate comprising:

a magnetizable layer;

a writeable layer; and

a single layer of adhesive destructively bonding said magnetizable layer and writeable layer together, said single layer of adhesive comprising at least 90 wt % of a polyurethane, said adhesive being a flexible, solid, heat resistant, durable, non-tack, and non-reversibly cross-linked virtually thermoset polymer,

wherein said magnetizable laminate is cured in a manner so that the single layer of adhesive is cured between said magnetizable layer and said writeable layer,

wherein said single layer of adhesive is resistant to transfer from the flexible magnetizable laminate to the cutting blades during cutting and resistant to delamination during use in direct sunlight when cured; and

wherein said single layer of adhesive has a thickness of 0.6 mil to 1.5 mil.

2. The system according to claim 1 wherein said single layer of adhesive comprises at least 95 wt % of said polyurethane.

3. The system according to claim 1 wherein said single layer of adhesive comprises 95-99 wt % of a polyurethane prepolymer and 1-3 wt % of methylene bisphenyl isocyanate.

4. The system according to claim 1 wherein said single layer of adhesive comprises compounded polyisobutylene rubber.

5. The system according to claim 1 , wherein said single layer of adhesive is solvent-free.

6. The system according to claim 1 , wherein said single layer of adhesive is flexible at room temperature.

7. The system according to claim 1 , wherein said single adhesive layer has a structure or arrangement resulting when formed by applying the adhesive at 250° F. at the viscosity of 13,000 centipoise onto the writeable layer.

8. A method of manufacturing a flexible magnetizable laminate having a single layer of adhesive for preventing delamination of said magnetizable laminate exposed to direct sunlight and preventing fouling of cutting blades during cutting of magnetizable laminates, said method comprising the steps of:

supplying a writeable layer;

applying said single layer of adhesive heated to 250° F. with a viscosity of 13,000 centipoise onto said writeable layer, said layer of adhesive having a thickness of 0.6 mil to 1.5 mil;

supplying a magnetizable layer;

laminating said writeable and magnetizable layers together with said single layer of adhesive, said single layer of adhesive comprises at least 90 wt % of a polyurethane; and

curing said single layer of adhesive between said writeable layer and said magnetizable layer to obtain a flexible, solid, heat resistant, durable, non-tacky, and non-reversibly crosslinked virtually thermoset polyurethane adhesive layer between said writeable and magnetizable layers,

wherein said single layer of adhesive is resistant to transfer from the at least one flexible magnetizable laminate to the cutting blades during cutting and resistant to delamination during use in direct sunlight when cured.

9. The method according to claim 8 wherein said single layer of adhesive comprises 95-99 wt % of a polyurethane prepolymer and 1-3 wt % of methylene bisphenyl isocyanate.

10. The method according to claim 8 , wherein said single layer of adhesive is solvent-free.

11. The method according to claim 8 , wherein said single layer of adhesive is flexible at room temperature.

12. The method according to claim 8 , wherein during a first stage the writeable layer is cooled after applying the heated adhesive to the writeable layer, and then during a second stage the magnetizable layer and writeable layer are joined together while adding heat to make the flexible magnetizable laminate.

13. A flexible magnetizable laminate system, comprising:

a flexible magnetizable laminate comprising at least two layers, the at least two layers comprising a writeable layer and a magnetizable layer; and

a cured single layer of adhesive located between the at least two layers, the cured adhesive structured and arranged to destructively bond the at least two layers together, the adhesive comprising at least 90 wt % of a polyurethane that is a flexible, solid, heat resistant, durable, non-tack, and non-reversibly cross-linked virtually thermoset polymer, the cured adhesive being resistant to transfer from the at least one flexible magnetizable laminate to cutting blades during cutting of the at least one flexible magnetizable laminate and resistant to delamination during use in direct sunlight,

wherein the single layer of adhesive has a thickness of 0.6 mil to 1.5 mil.

14. The system according to claim 13 wherein said single layer of adhesive comprises 95-99 wt % of a polyurethane prepolymer and 1-3 wt % of methylene bisphenyl isocyanate.

15. The system according to claim 13 , wherein said single adhesive layer has a cured structure or arrangement resulting when formed by applying the adhesive at 250° F. at a viscosity of 13,000 centipoise onto the writeable layer.

16. The system according to claim 13 , wherein said single adhesive layer has a structure or arrangement resulting when formed by applying the adhesive at 250° F. at a viscosity of 13,000 centipoise onto the writeable layer, and then cooling followed by joining the writeable layer and magnetizable layer together while adding heat to make the flexible magnetizable laminate.

17. A method of manufacturing a flexible magnetizable laminate, the method comprising the steps of:

providing a magnetizable layer;

providing a writeable layer;

providing an adhesive comprising at least 90 wt % polyurethane;

increasing the temperature of the adhesive to 250° F. to thin the adhesive to a viscosity of 13,000 centipoise;

applying a single layer of the thinned adhesive onto the writeable layer, the adhesive layer having a thickness of 0.6 mil to 1.5 mil;

laminating the magnetizable layer, single adhesive layer, and writeable layer together to form the flexible magnetic laminate;

applying pressure to the flexible magnetic laminate; and

curing the flexible magnetizable laminate so that the single layer of adhesive cures and destructively bonds the magnetizable and writeable layers together to form the flexible magnetizable laminate,

wherein the cured single layer of adhesive comprises a flexible, solid, heat resistant, durable, non-tacky, and non-reversibly cross-linked virtually thermoset polyurethane polymer; the cured single layer of adhesive being resistant to transfer from the flexible magnetizable laminate to the cutting blades during cutting of the flexible magnetizable laminate and resistant to delamination during use in direct sunlight.

18. The method according to claim 17 wherein said single layer of adhesive comprises 95-99 wt % of a polyurethane prepolymer and 1-3 wt % of methylene bisphenyl isocyanate.

19. The method according to claim 17 , wherein the writeable layer is cooled after applying heated adhesive to the writeable layer, and then the magnetizable layer and writeable layer are joined together while adding heat to make the flexible magnetizable laminate.