Gold-based alloy, free of silver and tin, for dental copings or abutments
Alloys and dental copings or abutments formed of alloys include 50-60 wt % gold, 5-14 wt % platinum, 0.1-3.0 wt % iridium and the remainder palladium. Other alloys and dental copings or abutments formed of alloys include 58 wt % gold, 10 wt % platinum, 1.0 wt % iridium, and 31 wt % palladium. The alloys are capable of withstanding temperature profiles during casting and multiple high temperature exposures of porcelain firing without excessive softening. The alloys also exhibit advantageous shear strain properties giving the alloys improved manufacturability characteristics.
1. A dental alloy for copings or abutments comprising 50-60 wt % gold, 5-14 wt % platinum, 0.1-3.0 wt % iridium and the remainder palladium, wherein the dental alloy is free of tin and silver and has a solidus temperature above 1425° C.
2. The dental alloy of claim 1 , wherein the dental alloy exhibits a torsional shear strain to fracture of greater than 4 units of shear strain.
3. The dental alloy of claim 1 , wherein palladium is present between 23-42 wt %.
4. The dental alloy of claim 1 , wherein palladium is present in the dental alloy in an amount of at least 30 wt %.
5. The dental alloy of claim 1 , wherein the dental alloy is wrought into bar, rod or wire form.
6. The dental alloy of claim 1 , wherein trace impurities of the dental alloy are below a total of 2000 ppm.
7. A dental alloy for copings or abutments comprising about 58 wt % gold, 10 wt % platinum, 1 wt % iridium, and 31 wt % palladium, wherein the dental alloy is free of tin and silver and has a solidus temperature above 1425° C.
8. A dental abutment including an alloy comprising 50-60 wt % gold, 5-14 wt % platinum, 0.1-3.0 wt % iridium and the remainder palladium, wherein the alloy is free of tin and silver and has a solidus temperature above 1425° C.
9. The dental abutment of claim 8 , wherein the alloy exhibits a torsional shear strain to fracture of greater than 4 units of shear strain.
10. The dental abutment of claim 8 , further comprising a cast on metal with or without a porcelain layer fused or otherwise fixed on the dental abutment.
11. The dental abutment of claim 8 , wherein palladium is present between 23-42 wt %.
12. The dental abutment of claim 8 , wherein palladium is present in the alloy in an amount of at least 30 wt %.
13. The dental abutment of claim 8 , wherein trace impurities of the alloy are below a total of 2000 ppm.
14. A dental abutment including an alloy comprising about 58 wt % gold, 10 wt % platinum, 1 wt % iridium, and 31 wt % palladium, wherein the alloy is free of tin and silver.