Security film and process for preparation thereof
View Patent ↗Disclosed herein are an anti-counterfeiting film and process for preparation thereof. The anti-counterfeiting film comprises a directional retroreflective layer ( 1 ), an optical-angle-based color-changing information layer ( 2 ), a reflective layer ( 3 ) and a support layer ( 4 ) which are combined in this turn. The support layer ( 4 ) is made of a polymer resin material, the reflective layer ( 3 ) is made of a material with high reflectivity and has a thickness of nanoscale, the information layer ( 2 ) is made of an optical-angle-based color-changing chiral polymer material having a helical structure or made of an optical-angle-based color-changing cellulose material. The optical-angle-based color-changing chiral polymer material having a helical structure is a condensation product of a chiral compound and a compound with functional group. The optical-angle-based color-changing cellulose material is composed of a cellulose derivative and a polymerisable monomer. The directional retroreflective layer ( 1 ) is composed of spheres which are made of optical material, and is spherically embedded in the support layer ( 4 ), wherein the refractive index of the material for the directional retroreflective layer ( 1 ) is 1.9-1.93.
1. An anti-counterfeiting film, comprising a directional retroreflective layer, an optical-angle-based color-changing information layer, a reflective layer and a support layer:
the support layer is made of a polymer resin material;
the reflective layer is made of a material having a high reflectivity and a thickness on a nanoscale;
the optical-angle-based color-changing information layer is made of an optical-angle-based color-changing chiral polymer material having a helical structure or of an optical-angle-based color-changing cellulose material, the optical-angle-based color-changing chiral polymer material having a helical structure is a condensation product of a chiral compound and a compound with a functional group;
the optical-angle-based color-changing cellulose material is composed of a cellulose derivative and a polymerisable monomer;
the directional retroreflective layer is composed of spheres which are made of optical material, and, the directional retroreflective layer is spherically embedded in the support layer; and
the refractive index of the material for the directional retroreflective layer is 1.9-1.93.
2. The anti-counterfeiting film according to claim 1 , wherein the polymer resin material for the support layer is selected from the group consisting of polyurethane, phenolic resin and polyacrylic acid resin.
3. The anti-counterfeiting film according to claim 1 , wherein the reflective layer is selected from the group consisting of ZnO, SnO, ZnS and TiO 2 .
4. The anti-counterfeiting film according to claim 1 , wherein the chiral compound is selected from the group consisting of isosorbide, D-camphoric acid, 2,3-dihydroxy butane and 3-methyl adipic acid;
the compound with a functional group is selected from the group consisting of hydroquinone, triglycol, p-hydroxybenzoic acid, ethylene glycol, oxalic acid, terephthalic acid, phenol, fatty acid and formaldehyde;
the cellulose derivative has the following structural formula:
wherein, Cell is cellulose, R is C 1 -C 20 alkyl or derivatives of phenyl;
the polymerisable monomer is selected from the group consisting of acrylate, methacrylate, vinyl ether, epoxy resin and cis-butyl diacid ester.
5. A process for preparation of the anti-counterfeiting film comprising the following steps:
coating a release material having adhesion force over a base film, implanting material for a directional retroreflective layer onto the release layer, followed by drying; and
coating or printing an optical-angle-based color-changing information layer over the directional retroreflective layer, then vapor depositing material for a reflective layer in a high vacuum, and coating material for a support layer over the reflective layer, followed by drying, then removing the base film and release layer to obtain the anti-counterfeiting film.
6. The process of claim 5 , wherein the coating step uses a technology selected from the group consisting of mesh coating, heat melting coating and blade coating is used for the coating.
7. The process of claim 5 , wherein the base film is selected from a transparent polymeric polyester film material.
8. The process of claim 7 , wherein the base film is selected from the group consisting of polyethylene terephthalate, polycarbonate, polystyrene and polyvinyl chloride.
9. The process of claim 5 , wherein the release material is liquid paraffin.
10. The process of claim 5 , wherein the printing step uses a technology selected from the group consisting of gravure printing, flexographic printing and screen printing is used for the printing.