Multilayer film using solvent-free adhesive, method for producing same and packaging container
A multilayered film which is formed using a solventless adhesive, can obviate wetting deficiency even when the film is manufactured by applying the solventless adhesive to a film by coating at a high speed, exhibits the excellent laminate strength and the excellent impact resistance after a liquid content is filled into a packaging container and exhibits excellent environment friendliness, a method of manufacturing the multilayered film, and a packaging container which uses the multilayered film are provided. In the multilayered film which is formed by laminating at least an inner-layer film, an adhesive layer and an outer-layer film in order, the adhesive layer is formed of a solventless adhesive which contains a polyester-based main agent and a curing agent made of aliphatic isocyanate and alicyclic isocyanate.
1. A multilayered film which is formed by laminating at least an inner-layer film, an adhesive layer and an outer-layer film in order, and
wherein the adhesive layer is formed of a solventless adhesive which contains a polyester-based main agent and a curing agent made of aliphatic isocyanate and alicyclic isocyanate,
wherein the curing agent of the solventless adhesive contains 1,6-hexamethylene diisocyanate (HDI) and 3-isocyanatomethyl-3,5,5-trimethyl cyclohexyl isocyanate (IPDI).
2. The multilayered film according to claim 1 , wherein viscosity of the solventless adhesive is 300 to 900 mPa·s/70° C.
3. The multilayered film according to claim 1 , wherein viscosity of the main agent of the solventless adhesive is 300 to 1000 mPa·s/70° C.
4. The multilayered film according to claim 1 , wherein a coating quantity of an adhesive in the adhesive layer is 1.5 to 3.5 g/m 2 .
5. The multilayered film according to claim 1 , wherein the outer layer film is formed of a polyamide-based or polyester-based biaxially oriented film.
6. The multilayered film according to claim 1 , wherein the inner layer film is formed of a polyolefin-based film.
7. The multilayered film according to claim 1 , wherein the multilayered film further includes one or more intermediate layers between the inner-layer film and the outer-layer film, and an adhesive layer is provided to at least one of portions between the respective layers.
8. A packaging container comprising the multilayered film according to claim 1 .
9. A method of manufacturing a multilayered film according to claim 1 , comprising the steps of:
preparing a solventless adhesive by heating a main agent and a curing agent and mixing the main agent and the curing agent to each other, wherein the curing agent of the solventless adhesive contains 1,6-hexamethylene diisocyanate (HDI) and 3-isocyanatomethyl-3,5,5-trimethyl cyclohexyl isocyanate (IPDI);
applying the solventless adhesive to either one of an inner layer film and an outer layer film by coating at a coating speed of 100 to 200 m/min; and
laminating either one of the inner layer film or the outer layer film to which the adhesive is not applied by coating to an adhesive surface of the film to which the adhesive is applied by coating while aligning either one of the inner layer film or the outer layer film with the adhesive surface.
10. The method of manufacturing a multilayered film according to claim 9 , wherein the viscosity of the solventless adhesive is 300 to 900 mPa·s/70° C.