Back sheet of solar cell and manufacturing method thereof
A back sheet of solar module with high adhesivity comprises a substrate ( 3 ), a layer of fluorine-based film ( 2 ), and a layer of fluoro-silicone film ( 1 ) or titanium-silicon film ( 4 ) formed between the layer of fluorine-based film ( 2 ) and the substrate ( 3 ), as well as on outer surface of the layer of fluorine-based film ( 2 ). A method for manufacturing the back sheet of solar module comprises the treatment on the layer of fluorine-based film ( 2 ) and/or substrate ( 3 ) with compound of fluoro-silicone or titanium-silicon, so as to coat a layer of fluoro-silicone film ( 1 ) or titanium-silicon film ( 4 ).
1. A back sheet for attachment to a solar module comprising
a substrate,
a layer of fluorine-based film defining a top surface and a bottom surface, one of which faces toward the substrate, and
fluoro-silicone material associated with the fluorine-based film and appearing at the top and bottom surfaces of the film, wherein the layer of fluorine-based film is tetrafluoroethylene homopolymer, a ternary copolymer, or chlorotrifluoroethylene, and wherein said ternary copolymer includes C 2 F 4 , C 3 F 6 , and PVDF, such that when the back sheet is attached to said solar module the fluoro-silicone material is in direct contact with said solar module.
2. The back sheet as defined in claim 1 , wherein said substrate is a substrate of PET, a substrate of a PET alloy, or a substrate of a PET composite.
3. The back sheet as defined in claim 2 , wherein said PET alloy is melt blended PET and PBT or melt blended PET and PEN with PBT or PEN of said PET alloy being 1-50 parts by mass.
4. The back sheet as defined in claim 2 , wherein said PET composite includes an inorganic oxide selected from SiO 2 , TiO 2 , Al 2 O 3 or ZrO 2 , with said PET composite being 1-35 parts by mass of said inorganic oxide.
5. The back sheet as defined in claim 1 , wherein said substrate is (a) fine closed-module foam layer or (b) closed-module foamed PET having a fine closed-module foam layer with foam holes having closed and ultra fine structures.
6. The back sheet as defined in claim 1 , wherein a thickness of said substrate is 0.1 to 10 mm.
7. The back sheet as defined in claim 1 , wherein a content of fluororesin in said layer of fluorine-based film is 30-95 parts by mass.
8. The back sheet as defined in claim 1 , the back sheet consisting essentially of: the first-mentioned layer of fluorine-based film, the first-mentioned fluoro-silicone material associated with the first-mentioned film, the substrate, a second layer of fluorine-based film defining a top surface and a bottom surface, and fluoro-silicone material being associated with the second film and appearing at the top and bottom surfaces of the second film.
9. The back sheet as defined in claim 1 , the back sheet consisting essentially of: the layer of fluorine-based film, the fluoro-silicone material appearing at the top and bottom surfaces of the film, and the substrate.
10. The back sheet as defined in claim 1 , the back sheet consisting essentially of: the layer of fluorine-based film, the fluoro-silicone material, and the substrate, the substrate defining a top surface and a bottom surface with the film on one of the top surface or bottom surface of the substrate, the fluoro-silicone material appearing at the other of the top surface or bottom surface of the substrate.
11. A back sheet for attachment to a solar module, comprising
a substrate,
a layer of fluorine-based film defining a top surface and a bottom surface, one of which faces toward the substrate,
a layer of titanium-silicon film comprising a titanium-silicon material associated with the flourine-based film and appearing at the top and bottom surfaces of the film, such that when the back sheet is attached to said solar module the titanium-silicon material is in direct contact with said solar module the layer of titanium-silicon film having a thickness of 0.01 to 5 μm.
12. The back sheet as defined in claim 11 , wherein said substrate is a substrate of PET, a substrate of a PET alloy, or a substrate of a PET composite.
13. The back sheet as defined in claim 12 , wherein said PET alloy is melt blended PET and PBT or melt blended PET and PEN with PBT or PEN of said PET alloy being 1-50 parts by mass.
14. The back sheet as defined in claim 12 , wherein said PET composite includes an inorganic oxide selected from SiO 2 , TiO 2 , Al 2 O 3 or ZrO 2 , with said PET composite being 1-35 parts by mass of said inorganic oxide.
15. The back sheet as defined in claim 11 , wherein said substrate is (a) fine closed-module foam layer or (b) closed-module foamed PET having a fine closed-module foam layer with foam holes having closed and ultra fine structures.
16. The back sheet as defined in claim 11 , wherein said layer of fluorine-based film is tetrafluoroethylene, a ternary copolymer or chlorotrifluoroethylene, and wherein said ternary copolymer includes C 2 F 4 , C 3 F 6 , and PVDF.
17. The back sheet as defined in claim 11 , the back sheet consisting essentially of: the first-mentioned layer of fluorine-based film, the first-mentioned titanium-silicon material associated with the first-mentioned layer of fluorine-based film, the substrate, a second layer of fluorine-based film defining a top surface and a bottom surface, and titanium-silicon material being associated with the second film and appearing on the top and bottom surfaces of the second film.
18. The back sheet as defined in claim 11 , the back sheet consisting essentially of: the layer of fluorine-based film, the titanium-silicon material, and the substrate, the substrate defining a top surface and a bottom surface with the film on one of the top surface or bottom surface of the substrate, and the titanium-silicon material appearing at the other of the top surface or bottom surface of the substrate.
19. The back sheet as defined in claim 11 , wherein the titanium-silicon material is an organic compound.