Graphene substituted with boron and nitrogen, method of fabricating the same, and transistor having the same
Graphene, a method of fabricating the same, and a transistor having the graphene are provided, the graphene includes a structure of carbon (C) atoms partially substituted with boron (B) atoms and nitrogen (N) atoms. The graphene has a band gap. The graphene substituted with boron and nitrogen may be used as a channel of a field effect transistor. The graphene may be formed by performing chemical vapor deposition (CVD) method using borazine or ammonia borane as a boron nitride (B—N) precursor.
1. Graphene, comprising:
a structure of carbon (C) atoms partially substituted with boron (B) atoms and nitrogen (N) atoms, wherein the graphene has a band gap.
2. The graphene of claim 1 , wherein the B atoms and the N atoms substitute from about 1% to about 20% of the C atoms of the graphene.
3. The graphene of claim 1 , wherein a difference between densities of the B atoms and the N atoms is below 10 13 cm −2 .
4. The graphene of claim 3 , wherein the B atoms and the N atoms are present in the graphene at substantially at the same ratio.
5. The graphene of claim 4 , wherein the C atoms of the graphene are partially substituted with at least one dimer having one of the B atoms and one of the N atoms or at least one hexagonal structure having three of the B atoms and three of the N atoms.
6. The graphene of claim 1 , wherein the band gap is about 0.05 eV to about 0.3 eV.
7. The graphene of claim 1 , wherein each of the boron atoms is bonded to at least one of the nitrogen atoms.
8. The graphene of claim 4 , wherein the C atoms of the graphene are partially substituted with at least one B—N heterodimer.
9. The graphene of claim 4 , wherein the C atoms of the graphene are partially substituted with at least one heterocyclic structure having three of the B atoms and three of the N atoms.
10. The graphene according to claim 1 , wherein the graphene is in a channel of a transistor.
11. The graphene of claim 10 , wherein the B atoms and the N atoms substitute from about 1% to about 20% of the C atoms of the graphene.
12. The graphene of claim 10 , wherein a difference between densities of the B atoms and the N atoms is below 10 13 cm −2 .
13. The graphene of claim 12 , wherein the B atoms and the N atoms are present in the graphene at substantially the same ratio.
14. The graphene of claim 13 , wherein the C atoms of the graphene are partially substituted with at least one dimer having one of the B atoms and one of the N atoms or at least one hexagonal structure having three of the B atoms and three of the N atoms.
15. A method of fabricating graphene substituted with boron and nitrogen, comprising:
forming the graphene according to claim 1 by performing a chemical vapor deposition (CVD) method using borazine or ammonia borane as a B-N precursor.
16. The method of claim 15 , wherein the B atoms and the N atoms substitute from about 1% to about 20% of the C atoms of the graphene.
17. The method of claim 15 , wherein the B atoms and the N atoms are present in the graphene at substantially the same ratio.
18. The method of claim 17 , wherein the B-N precursor is a dimer having one of the B atoms and one of the N atoms or a hexagonal structure having three of the B atoms and three of the N atoms.