Decorative laminate and method for manufacturing same
A decorative laminate includes a decorative layer and a core layer. The decorative layer is composed of a resin impregnated decorative sheet. The core layer is composed of at least one resin impregnated sheet of core paper. The core paper is impregnated with a resin composed of phenol formaldehyde resin and wood molasses. In this manner, a substantial portion of the resin used to impregnate the core paper is replaced with wood molasses, which results in a reduction of the cost of manufacturing the decorative laminate. The decorative laminate is manufactured by preparing a resin impregnated decorative sheet and preparing at least one resin impregnated core sheet by impregnating a core sheet with a resin composition composed of phenol formaldehyde resin and wood molasses. The decorative sheet and the core sheet are then layered to form a laminate lay-up that is heated and pressed to consolidate and cure the laminate.
1. A decorative laminate, comprising:
a decorative layer including a resin impregnated decorative sheet; and
a core layer including at least one resin impregnated sheet of core paper, wherein the core paper is impregnated with a resin composed of phenol formaldehyde resin and wood molasses.
2. The decorative laminate of claim 1 , wherein the core paper is impregnated with a resin composed of at least 5% by weight molasses.
3. The decorative laminate of claim 2 , wherein the core paper is impregnated with a resin composed of 60% by weight phenol formaldehyde and 40% by weight molasses.
4. The decorative laminate of claim 2 , wherein the core paper is Kraft paper.
5. The decorative laminate of claim 1 , wherein the core paper is impregnated to a saturation content in a range of 25.0% to 50.0%.
6. The decorative laminate of claim 5 , wherein the core paper is impregnated to a saturation content in a range of 28.0% to 35.0%.
7. The decorative laminate of claim 1 , wherein the decorative sheet is impregnated with melamine resin.
8. The decorative laminate of claim 1 , further including an overlay paper layer positioned over the decorative layer.
9. The decorative laminate of claim 1 , wherein the core paper is Kraft paper.
10. The decorative laminate of claim 1 , wherein the Kraft paper has a dry weight of 160-550 grams/meter 2 .
11. The decorative laminate of claim 1 , wherein the core paper is impregnated to a saturation content in a range of 25.0% to 50.0%.
12. The decorative laminate of claim 10 , wherein the core paper is impregnated to a saturation content in a range of 28.0% to 35.0%.
13. A method of manufacturing decorative laminate, said method comprising:
preparing a resin impregnated decorative sheet;
preparing at least one resin impregnated core sheet by impregnating a core sheet with a resin composition composed of phenol formaldehyde resin and wood molasses;
layering the resin impregnated decorative sheet and the at least one resin impregnated core sheet to form a laminate lay-up; and
heating and pressing the laminate lay-up to consolidate and cure the laminate.
14. The method of claim 13 , wherein the resin composition is composed of at least 5% by weight wood molasses.
15. The method of claim 13 , which further includes preparing the resin composition by adding an alkaline material to the wood molasses until a pH of the wood molasses matches a pH of the phenol formaldehyde resin, thereby creating pH1 adjusted wood molasses, and incorporating the pH adjusted wood molasses into the phenol formaldehyde creating a phenol formaldehyde resin/wood molasses composition.
16. The method of claim 15 , wherein the pH adjusted wood molasses has a pH of 8.5.
17. The method of claim 15 , wherein the alkaline material is NaOH.
18. The method of claim 15 , wherein the resin composition is composed of at least 5% by weight wood molasses.
19. The method of claim 15 , wherein preparing the resin composition further includes adjusting the solid content of the phenol formaldehyde resin/wood molasses composition to a range of 57% to 62% to create the resin composition.
20. The method of claim 13 , wherein the core paper is impregnated with a resin composed of 60% by weight phenol formaldehyde and 40% by weight molasses.