Light diffusing fibers and methods for making the same
Light diffusing optical fibers and methods for producing light diffusing optical fibers are disclosed. In one embodiment, a light diffusing optical fiber includes a core portion formed from silica glass and comprising a plurality of helical void randomly distributed in the core portion of the optical fiber and wrapped around the long axis of the optical fiber. A pitch of the helical voids may vary along the axial length of the light diffusing optical fiber in order to achieve the desired illumination along the length of the optical fiber. A cladding may surround the core portion. Light guided by the core portion is scattered by the helical voids radially outward, through the cladding, such that the light diffusing optical fiber emits light with a predetermined intensity over an axial length of the light diffusing optical fiber, the light diffusing optical fiber having a scattering induced attenuation loss greater than about 0.2 dB/m at a wavelength of 550 nm.
1. A light diffusing optical fiber for use in an illumination device, the light diffusing optical fiber comprising:
a core portion formed from silica-based glass and comprising helical voids randomly distributed in the core portion and wrapped around a long axis of the light diffusing optical fiber such that an angle between the long axis and the helical voids is non-zero, a pitch of the helical voids varying along an axial length of the light diffusing optical fiber; and
a cladding surrounding and in direct contact with the core portion, wherein light guided by the core portion is scattered by the helical voids radially outward and through the cladding such that the light diffusing optical fiber emits light with a predetermined intensity over the axial length of the light diffusing optical fiber, the light diffusing optical fiber having a scattering induced attenuation loss greater than about 0.2 dB/m at a wavelength of 550 nm.
2. The light diffusing optical fiber of claim 1 , wherein the scattering induced attenuation loss is greater than about 0.5 dB/m at a wavelength of 550 nm.
3. The light diffusing optical fiber of claim 1 , wherein the helical voids are formed in a nano-structured ring centered on the long axis of the light diffusing optical fiber and surrounding an inner core portion comprising solid glass, the nano-structured ring having a radial thickness of at least 2 μm.
4. The light diffusing optical fiber of claim 3 , wherein the inner core portion has an index of refraction n 1 and the nano-structured ring has an index of refraction n 2 such that n 1 >n 2 .
5. The light diffusing optical fiber of claim 3 , wherein the cladding is in direct contact with the nano-structured ring.
6. The light diffusing optical fiber of claim 3 , wherein the nano-structured ring is surrounded by an outer core portion comprising solid glass.
7. The light diffusing optical fiber of claim 6 , wherein the inner core portion has an index of refraction n 1 , the nano-structured ring has an index of refraction n 2 and the outer core portion has an index of refraction n 3 such that n i and n 3 are greater than n 2 .
8. The light diffusing optical fiber of claim 1 , wherein the helical voids have a diameter less than or equal to about 1 μm.
9. The light diffusing optical fiber of claim 1 , wherein the axial length of the light diffusing optical fiber is less than about 100 meters.
10. The light diffusing optical fiber of claim 1 , wherein the core portion of the light diffusing optical fiber has a radius greater than or equal to 10 μm and less than or equal to 600 μm.
11. The light diffusing optical fiber of claim 1 , wherein the cladding has a radial thickness of at least 10 μm.
12. The light diffusing optical fiber of claim 1 , wherein the light diffusing optical fiber is a multimode fiber having a numerical aperture greater than or equal to about 0.3.
13. The light diffusing optical fiber of claim 1 , further comprising at least one coating layer surrounding and in direct contact with the cladding.
14. A method for producing a light diffusing optical fiber, the method comprising:
forming an optical fiber preform comprising a preform core portion having randomly distributed voids;
drawing the optical fiber preform into an optical fiber such that the randomly distributed voids are drawn into elongated voids that are substantially parallel to a long axis of the optical fiber;
rotating the optical fiber about the long axis of the optical fiber such that, after rotating, the elongated voids are helical voids wrapped around the long axis of the light diffusing optical fiber such that an angle between the long axis and the helical voids is non-zero.
15. The method of claim 14 , wherein the optical fiber is rotated about the long axis of the optical fiber while the optical fiber is molten.
16. The method of claim 14 , further comprising coating the optical fiber with at least one coating layer before the optical fiber is rotated about the long axis of the optical fiber.
17. The method of claim 14 , wherein the optical fiber preform further comprises a preform cladding portion surrounding and in direct contact with the preform core portion.
18. A light diffusing optical fiber for use in an illumination device, the light diffusing optical fiber comprising:
a core portion formed from silica-based glass and comprising helical voids randomly distributed in the core portion and wrapped around a long axis of the light diffusing optical fiber such that an angle between the long axis and the helical voids is non-zero, a pitch of the helical voids varying along an axial length of the light diffusing optical fiber; and
a cladding surrounding and in direct contact with the core portion, wherein light guided by the core portion is scattered by the helical voids radially outward and through the cladding such that the light diffusing optical fiber emits light with a predetermined intensity over the axial length of the light diffusing optical fiber, the light diffusing optical fiber having a scattering induced attenuation loss greater than about 0.2 dB/m at a wavelength of 550 nm, wherein the pitch of the helical voids is less than 0.20 m.
19. A light diffusing optical fiber for use in an illumination device, the light diffusing optical fiber comprising:
a core portion formed from silica-based glass and comprising helical voids randomly distributed in the core portion and wrapped around a long axis of the light diffusing optical fiber such that an angle between the long axis and the helical voids is non-zero, a pitch of the helical voids varying along an axial length of the light diffusing optical fiber; and
a cladding surrounding and in direct contact with the core portion, wherein light guided by the core portion is scattered by the helical voids radially outward and through the cladding such that the light diffusing optical fiber emits light with a predetermined intensity over the axial length of the light diffusing optical fiber, the light diffusing optical fiber having a scattering induced attenuation loss greater than about 0.2 dB/m at a wavelength of 550 nm, wherein the pitch of the helical voids is less than or equal to 0.20 m and greater than or equal to 0.01 m.
20. A light diffusing optical fiber for use in an illumination device, the light diffusing optical fiber comprising:
a core portion formed from silica-based glass and comprising helical voids randomly distributed in the core portion and wrapped around a long axis of the light diffusing optical fiber such that an angle between the long axis and the helical voids is non-zero, a pitch of the helical voids varying along an axial length of the light diffusing optical fiber; and
a cladding surrounding and in direct contact with the core portion, wherein light guided by the core portion is scattered by the helical voids radially outward and through the cladding such that the light diffusing optical fiber emits light with a predetermined intensity over the axial length of the light diffusing optical fiber, the light diffusing optical fiber having a scattering induced attenuation loss greater than about 0.2 dB/m at a wavelength of 550 nm, wherein the pitch of the helical voids increases from an input end of the light diffusing optical fiber to an output end of the light diffusing optical fiber.