Slow calcium release fertilizer
Slow calcium release fertilizers and methods for their synthesis are described. Organic materials, particularly from manure are used for coating to achieve slow release forms of the fertilizer. Desirably, low temperature kinetic treatments are used to prepare pulverized forms having small size yet well coated with natural (non-denatured) molecular material to achieve the slow release. A desired embodiment is made from kinetic processing of rock gypsum and manure at low temperatures with added acid. Use of the fertilizers leads to acceleration of microbial viability.
1. A method of preparing a slow release calcium biotic fertilizer, comprising:
combining rock gypsum and manure in a mixer in the absence of an added chemical or heat to form rock gypsum particles coated with manure;
adding water and acid to the coated gypsum particles to substantially convert carboxylate anions on the particle surfaces into their protonated form; and
drying the coated gypsum particles at a temperature below the boiling point of water.
2. The method of claim 1 , wherein the rock gypsum and manure are combined in a kinetic processor.
3. The method of claim 2 , wherein the rock gypsum is pulverized in the kinetic mixer during the step of combining the calcium mineral with manure.
4. The method of claim 1 , wherein the manure is chicken manure.
5. The method of claim 1 , wherein acid is added to a final ratio of between 20 pounds and 200 pounds of 95% sulfuric acid per 4000 pounds of manure and the manure has a water content of between 10 and 30 percent.
6. The method of claim 1 , wherein the drying step for drying the coated gypsum particles heats the particles to about 175-190 degrees Fahrenheit for about 15 to 35 minutes.