Coating composition and method for producing the same, coating film and underwater structures
Provided are coating composition containing an organic polymer particle (A) composed of an organic polymer having a hydroxyl group and a cationic group in a molecule, the weight average particle size of which being 10 to 35 μm, and a base resin (B), wherein the content of the organic polymer particle (A) is 0.5 to 5.0% by weight in the solid content of the coating composition, and a method of producing the same, and a coating film and underwater structure using the coating composition. The base resin (B) has a group represented by the following general formula (1): —COO-M-OCO-A (1) (wherein, M represents a divalent or higher valent metal, and A represents an organic acid residue of monobasic acid) or a group represented by the following general formula (2): —COO—Si(R 1 R 2 R 3 ) (2) (wherein, R 1 , R 2 and R 3 , which may be the same or different, represent an isopropyl group or an n-butyl group) in a side chain, or has a cross-linking structure represented by the following general formula (3): —COO-M-OCO— (3) (wherein, M represents the same meaning as described above).
1. A coating composition comprising:
an organic polymer particle (A) composed of an organic polymer having a hydroxyl group and a cationic group in a molecule, said organic polymer particle (A) having a weight average particle size of 10 to 35 μm, as measured by using a laser diffraction-type particle size distribution measuring apparatus, and
a base resin (B) having at least any one of a group represented by the following general formula (1):
—COO-M-OCO-A (1)
(wherein, M represents a divalent or higher valent metal, and A represents an organic acid residue of monobasic acid) and a group represented by the following general formula (2):
—COO—Si(R 1 R 2 R 3 ) (2)
(wherein, R 1 , R 2 and R 3 , which may be the same or different from one another, represent an isopropyl group or an n-butyl group) in a side chain, or having a cross-linking structure cross-linking between main chains, represented by the following general formula (3):
—COO-M-OCO (3)
(wherein, M represents the same meaning as described above),
wherein the content of said organic polymer particle (A) is 0.5 to 5.0% by weight in the solid content of the coating composition.
2. The coating composition according to claim 1 , wherein said cationic group is an amino group or an amide group.
3. The coating composition according to claim 2 , wherein said organic polymer is at least one kind selected from the group consisting of chitin, chitosan and derivatives thereof.
4. The coating composition according to claim 1 , wherein said base resin (B) contains an acrylic resin having the group represented by said general formula (1) in a side chain.
5. The coating composition according to claim 1 , wherein said base resin (B) contains a resin having at least any one of the group represented by said general formula (1) and the group represented by said general formula (2) in a side chain, and having a cross-linking structure represented by said general formula (3) that cross-links between main chains.
6. A method of producing a coating composition comprising the step of: mixing an organic polymer particle (A) composed of an organic polymer having a hydroxyl group and a cationic group in a molecule, said organic polymer particle (A) having a weight average particle size of 10 to 35 μm, as measured by using a laser diffraction-type particle size distribution measuring apparatus; and
a base resin (B) having at least any one of a group represented by the following general formula (1):
—COO-M-OCO-A (1)
(wherein, M represents a divalent or higher valent metal, and A represents an organic acid residue of monobasic acid) and a group represented by the following general formula (2):
—COO—Si(R 1 R 2 R 3 ) (2)
(wherein, R 1 , R 2 and R 3 , which may be the same or different from one another, represent an isopropyl group or an n-butyl group) in a side chain, or having a cross-linking structure cross-linking between main chains, represented by the following general formula (3):
—COO-M-OCO (3)
(wherein, M represents the same meaning as described above) so that the content of said organic polymer particle (A) is 0.5 to 5.0% by weight in the solid content of the coating composition.
7. A coating film formed from the coating composition according to claim 1 .
8. An underwater structure having a coating film formed from the coating composition according to claim 1 .
9. A marine vessel having a coating film formed from the coating composition according to claim 1 .