Abrasive grain agglomerates, process for the production thereof and the use thereof for producing abrasives
View Patent ↗The present invention relates to abrasive grain agglomerates composed of fine-particle primary abrasive grains which are held together by means of a binder based on an aluminosilicate having a molar ratio of Al 2 O 3 to SiO 2 of from 1:2 to 1:20. The particular advantage of these abrasive grain agglomerates is that the binder cures fully at below 450° C., preferably below 400° C., to form abrasive grain agglomerates having an extraordinarily high strength.
1. An abrasive grain agglomerate comprising a multitude of primary abrasive grains, said abrasive grains are selected from the group consisting of corundum, fused corundum, sintered corundum, zirconium corundum, silicon carbide, boron carbide, cubic boron nitride, diamond and mixtures thereof bonded together with an inorganic binder into an abrasive grain agglomerate,
wherein the binder comprises,
about 1 to about 25% by weight of an alumina silicate,
about 20 to about 80% by weight of water glass and
about 41 to about 60% by weight of water; each weight relative to the total weight of the binder,
wherein a molar ratio of Al 2 O 3 to SiO 2 in the binder is from about 1:2 to about 1:20 and the binder is hardened at temperatures of ≦450° C.
2. The abrasive grain agglomerates according to claim 1 , wherein the binder further comprises a complex alkali fluoride, selected from the group consisting of Na 3 AlF 6 , K 2 NaAlF 6 , Na 2 SiF 6 , K 2 SiF 6 , NaBF 4 and KBF 4 , with a weight portion of the alkali fluoride, of about 1% by weight to about 15% by weight relative to the total weight of the binder.
3. The abrasive grain agglomerates according to claim 1 , wherein the binder further comprises a phosphate with a weight portion of about 20% by weight to about 60% by weight relative to the total weight of the binder.
4. The abrasive grain agglomerates according to claim 1 , wherein the portion constituting the binder is about 1 to about 15% by weight relative to the abrasive grains bonded to each other.
5. The abrasive grain agglomerates according to claim 1 , wherein the aluminum silicate is selected from the group consisting of meta kaolin, flue ash, smelting slag, rock dusts, fine sands and activated clays.
6. The abrasive grain agglomerates according to claim 5 , wherein the aluminum silicate is a three-dimensional network of SiO 4 - and AlO 4 -tetrahedrons generated through polycondensation from reactive Al 2 O 3 and SiO 2 .
7. The abrasive grain agglomerates according to claim 6 , wherein the three-dimensional network in addition includes PO 4 tetrahedrons.
8. The abrasive grain agglomerates according to claim 1 , wherein the binder further comprises at least one of: filler material and auxiliary abrasive agents selected from the group consisting of sulfides, phosphates, carbonates and/or halogen containing complex compounds selected from the group consisting of elements Na, Li, K, Mg, Ca, Al, Mn, Cu, Sn, Fe, Ti, Sb and Zn.
9. The abrasive grain agglomerates according to claim 8 , wherein the binder includes a portion of about 2% by weight to about 15% by weight fine grain selected from the group consisting of corundum, fused corundum, sinter corundum zirconium corundum, silicon carbide, boron carbide cubic boron nitride, diamond and mixtures thereof as a filler material, wherein the fine grain has an average grain size between about 0.5 μm and about 30 μm.
10. The abrasive grain agglomerates according to claim 9 , wherein the primary abrasive grain includes a bimodal grain distribution, wherein a difference in percent between an average grain size is between about 30% and about 70%.
11. The abrasive grain agglomerates according to claim 1 , wherein the average grain size of the primary particles is between 30 μm and 200 μm and the average diameter of an abrasive grain agglomerate is between 0.05 mm and 3 mm.
12. The abrasive grain agglomerates according to claim 1 , wherein porosity of an abrasive grain agglomerate is about 10% by volume to about 50% by volume.
13. The abrasive grain agglomerates according to claim 1 , wherein the abrasive grain agglomerates have a fracture resistance (CFF) according to Vollstädt of at least 10N, preferably at least 40N.