Anti-counterfeit film with an amphichroic pattern and a preparation method thereof
An anti-counterfeit film comprising an amphichroic pattern is prepared by (1) mixing a polymerizable liquid crystal material of chiral structure and a photoinitiator, blade-coating the mixture on a base film and then drying; (2) partially exposing the resulting material produced in step (1) using a positioned UV lamp, then drying and exposing in an UV radiation to obtain a desired film. The film prepared by the method has an amphichroic pattern which typically presents a red and green picture when being vertically observed, the original red and green respectively changes into green and blue when being observed at a certain incline angel. The anti-counterfeit film is characterized by obvious color change, easy identification, practicability and convenience, thus facilitating promotion and application.
1. A method for preparing an anti-counterfeit film having an amphichroic pattern, comprising:
(1) mixing a polymerizable liquid crystal material of chiral structure and a photoinitiator, heating the mixture to a temperature in the range of 80 to 120° C., blade-coating the mixture on a base film, and then drying the coated base film;
(2) subjecting the dried mixture to a local exposure of an ultraviolet lamp, followed by drying and another exposure to ultraviolet, to obtain an anti-counterfeit film having an amphichroic pattern;
wherein the said polymerizable liquid crystal material of chiral structure is a cholesteric siloxane liquid crystal.
2. The method according to claim 1 , wherein the said photoinitiator is one or more members selected from the group consisting of benzophenone, benzoyl peroxide, azobis(isobutyronitrile), 2-hydroxy-methylphenylpropane-1-one, 1-hydroxycyclohexylphenylketone or 2-methyl-1-(4-methylthiophenyl)-2-morpholinyl-1-propanone.
3. The method according to claim 2 , wherein the photoinitiator is used in an amount of between 2 and 10% by weight of the polymerizable liquid crystal material of chiral structure.
4. The method according to claim 1 , wherein the said base film is selected from the group consisting of a polycarbonate film, a polyester film or a polypropylene film.
5. The method according to claim 1 , wherein the said base film is coated with a polyimide-type liquid crystal orientation agent or treated with polyvinyl alcohol.
6. The method according to claim 1 , wherein the coating has a controlled thickness of from 2 to 15 μm.
7. The method of claim 1 , wherein the drying after local exposure to an ultraviolet lamp is at a temperature in the range of 80 to 120° C.
8. The method of claim 7 , wherein the drying after local exposure to an ultraviolet lamp is at a higher temperature than said heating temperature.
9. The method according to claim 7 , wherein the first local exposure is for an exposure time of 5 to 30 seconds and an exposure energy of from 1.5 to 15 mw/cm 2 , drying of the coated base film is for 0.5 to 2.5 minutes, and the second ultraviolet exposure is at an exposure time of 5 to 30 seconds and an exposure energy of 1.5 to 15 mw/cm2.