Ceramic material, method for producing said ceramic material and component comprising said ceramic material
The invention relates to a ceramic material of the formula [(Bi 0.5 Na 0.5 TiO 3 )( 1-y )(BaTiO 3 ) y ]( 1-x ) (K 0.5 Na 0.5 NbO 3 ) x , and also to a method for producing the same and to a component comprising said material.
1. A ceramic material comprising:
material having the formula [(Bi 0.5 Na 0.5 TiO 3 ) (1-y) (BaTiO 3 ) y ] (1-x) (K 0.5 Na 0.5 NbO 3 ) x , wherein 0<x≦0.12 and 0.1≦y≦0.5.
2. The. material according to claim 1 , said material being lead-free.
3. The material according to claim 1 , where x=0.09 and y=0.2.
4. The material according to claim 1 , where x=0.085 and y=0.3.
5. The material according to claim 1 , where x=0.075 and y=0.4.
6. The material according to claim 1 , where x=0.07 and y=0.5.
7. The material according to claim 1 , where x=0.06 and y=0.1.
8. A method for producing a ceramic material, the material having the formula [(Bi 0.5 Na 0.5 TiO 3 ) (1-y) (BaTiO 3 ) y ] (1-x) (K 0.5 Na 0.5 NbO 3 ) x , wherein 0<x≦0.12 and 0.1≦y≦0.5, said method comprising the following steps:
A) powdery oxygen-containing compounds of Bi, Na, K, Ti, Ba and Nb are mixed in a stoichiometric ratio to produce a starting mixture;
B) the starting mixture is ground and calcined to produce a powdery solid solution; and
C) the powdery solid solution is pressed and sintered.
9. The method according to claim 8 , wherein, in method. step A), starting materials are selected from a group comprising oxides and carbonates of Bi, Na, K, Ti, Ba and Nb.
10. The method according to claim 8 , wherein, in method step B), the starting mixture is ground in a solvent, dried and calcined at a temperature in the range of 800° C. to 950° C.
11. The method according to claim 8 , wherein, in method step C), the ground powdery solid solution is pressed to form disks and sintered at a temperature in the range of 1150° C. to 1200° C.
12. A component comprising at least one ceramic base body and at least two electrodes arranged on the base body, wherein the base body comprises: a ceramic material of the formula [(Bi 0.5 Na 0.5 TiO 3 ) (1-y) (BaTiO 3 ) y ] (1-x) (K 0.5 Na 0.5 NbO 3 ) x , where 0<x≦0.12 and 0.1≦y≦0.5.
13. The component according to claim 12 , wherein the base body comprises: a multiplicity of stacked layers, which comprise the ceramic material, with electrodes arranged therebetween, wherein the electrodes are electrically contacted via external electrodes arranged on the outer surface of the base body.
14. Use of the component according to claim 12 as an actuator.
15. Use of the component according to claim 12 as a sensor.