Graft polymerization method and product obtained thereby
View Patent ↗Disclosed is a graft polymerization method which has solved problems involved in use of a solvent, a radical initiator and high-energy radiation when a monomer is graft-polymerized on the surface of a polymer base. The graft polymerization method is characterized in that a polymerization product is obtained by immersing a polymer base (i) having a ketone group on the surface into a reaction system containing a monomer (ii) and then irradiating the polymer base (i) with light so that polymerization of the monomer starts from the surface of the polymer base (i).
1. A method of surface-initiated graft polymerization comprising:
immersing a polymer substrate (i) having a ketone group on the surface of the substrate in a reaction system containing a monomer (ii); and
irradiating the polymer substrate (i) with light which is an ultraviolet ray or visible ray, thereby initiating a polymerization reaction of the monomer from the surface of the polymer substrate (i) to give a polymerization product.
2. The method according to claim 1 , wherein a polymerization initiator is absent at the surface and inside of the polymer substrate (i) and in the reaction system containing the monomer (ii).
3. The method according to claim 1 , wherein the reaction system containing the monomer (ii) further contains a solvent in which the monomer (ii) is dispersible or dissolvable without dissolving the polymer substrate (i).
4. The method according to claim 1 , wherein the polymer substrate (i) is a polymer substrate comprising an aromatic ketone.
5. The method according to claim 1 , wherein the polymer substrate is selected from the group consisting of polyether ketone (PEK), polyether ether ketone (PEEK), polyether ketone ketone (PEKK), polyether ether ketone ketone (PEEKK), polyether ketone ether ketone ketone (PEKEKK) and polyacrylic ether ketone (PEAK).
6. The method according to claim 1 , wherein the monomer (ii) is selected from (meth)acrylate compounds.
7. The method according to claim 1 , wherein the monomer (ii) is at least a compound selected from the group consisting of epoxy(meth)acrylate compounds, urethane(meth)acrylate compounds, polyester(meth)acrylate compounds, polybutadiene(meth)acrylate compounds and silicone (meth)acrylate compounds.
8. The method according to claim 1 , wherein the monomer (ii) contains a compound having a phosphorylcholine group.
9. The method according to claim 8 , wherein the compound having a phosphorylcholine group is 2-methacryloyloxyethyl phosphorylcholine (MPC).
10. The method according to claim 1 , wherein the irradiated light has a wavelength in the range from 200 to 450 nm.
11. The method according to claim 1 , wherein the irradiated light has a wavelength in the range from 300 to 400 nm.
12. The method according to claim 1 , wherein the light has a wavelength in a range from 200 nm to 450 nm.