Method for manufacturing nonaqueous secondary battery electrode
A method is provided for manufacturing an electrode that has a porous inorganic layer on the surface of an active material layer and is suitable for constructing a nonaqueous secondary battery with excellent input-output performance. In this manufacturing method, an electrode perform, which has an active material layer ( 344 ) consisting primarily of active material particles ( 42 ) and supported on a collector ( 342 ), is prepared. The water concentration of at least the surface ( 344 a ) of the active material layer ( 344 ) is adjusted to 100 ppm to 500 ppm. A slurry (S) containing inorganic particles ( 44 ), a binder and an organic solvent is coated on the surface ( 344 a ) of the active material layer with the water concentration thus adjusted, to form a porous inorganic layer.
1. A method for manufacturing a nonaqueous secondary battery negative electrode having a porous inorganic layer on a negative electrode active material layer, the method comprising the following steps performed in the sequence set forth:
preparing a negative electrode preform that has a negative electrode active material layer consisting primarily of negative electrode active material particles and supported on a collector, wherein the negative electrode active material layer is prepared by applying a liquid composition containing the negative electrode active material particles dispersed in a water-based solvent to the collector, and drying the liquid composition;
adjusting a water concentration of the negative electrode active material layer so that a water concentration of at least the surface of the negative electrode active material layer is 100 ppm to 500 ppm, wherein the adjustment of the water concentration of the negative electrode active material layer is performed separately from the preparation of the negative electrode preform; and
coating a slurry containing inorganic particles, a binder and an organic solvent on the surface of the negative electrode active material layer with the water concentration thus adjusted, to form a porous inorganic layer.
2. The method according to claim 1 , wherein the organic solvent is an amide solvent.
3. The method according to claim 2 , wherein the amide solvent is N-methyl-2-pyrrolidone.
4. The method according to claim 1 , wherein the binder is an acrylic binder.
5. The method according to claim 1 , wherein the inorganic particles are alumina particles.
6. The method according to claim 1 , wherein the negative electrode active material particles are carbon particles.
7. The method according to claim 1 , wherein treatment to introduce hydrophilic functional groups on the surface of the negative electrode active material particles located in a surface part of the negative electrode active material layer is performed prior to the adjustment of the water concentration.
8. The method according to claim 7 , wherein the treatment to introduce hydrophilic functional groups comprises bringing a lower alcohol into contact with the surface part of the negative electrode active material layer.
9. The method according to claim 1 , wherein the adjustment of the water concentration of the negative electrode active material layer comprises retaining the negative electrode active material layer in an environment having dew point of −10° C. or more.
10. A method for manufacturing a lithium-ion battery , comprising constructing a lithium-ion battery using a negative electrode manufactured by the method according to claim 1 .
11. A vehicle equipped with a lithium-ion battery manufactured by the method according to claim 10 .
12. The method according to claim 1 , further comprising performing a treatment to introduce hydrophilic functional groups on the surface of the negative electrode active material particles located in a surface part of the negative electrode active material layer prior to the adjustment of the water concentration, but after the preparation of the negative electrode preform.
13. The method according to claim 1 , further comprising spraying a lower alcohol to a surface part of the negative electrode active material layer prior to the adjustment of the water concentration.
14. The method according to claim 1 , further comprising dipping a lower alcohol to a surface part of the negative electrode active material layer prior to the adjustment of the water concentration.
15. A method for manufacturing a nonaqueous secondary battery negative electrode having a porous inorganic layer on a negative electrode active material layer, comprising the following steps performed in the sequence set forth:
preparing a negative electrode preform that has a negative electrode active material layer consisting primarily of negative electrode active material particles and supported on a collector, wherein the negative electrode active material layer is prepared by applying a liquid composition containing the negative electrode active material particles dispersed in a water-based solvent to the collector, and drying the liquid composition;
performing a treatment to introduce hydrophilic functional groups on the surface of the negative electrode active material particles located in a surface part of the negative electrode active material layer after the preparation of the negative electrode preform,
adjusting a water concentration of the negative electrode active material layer so that a water concentration of at least the surface of the negative electrode active material layer is 100 ppm to 500 ppm, wherein the adjustment of the water concentration of the negative electrode active material layer is performed separately from the preparation of the negative electrode preform; and
coating a slurry containing inorganic particles, a binder and an organic solvent on the surface of the negative electrode active material layer with the water concentration thus adjusted, to form a porous inorganic layer.
16. The method according to claim 15 , wherein the treatment to introduce hydrophilic functional groups comprises bringing a lower alcohol into contact with the surface part of the negative electrode active material layer.
17. The method according to claim 1 , wherein the preparation of the negative electrode preform is performed under an environment having dew point of −30° C. or lower, and the adjustment of the water concentration of the negative electrode active material layer comprises retaining the negative electrode active material layer in an environment having dew point of −10° C. or more.
18. The method according to claim 1 , wherein the adjustment of the water concentration of the negative electrode active material layer comprises retaining the negative electrode active material layer in an environment having dew point from −10° C. to +10° C.
19. The method according to claim 1 , wherein the adjustment of the water concentration of the negative electrode active material layer is performed such that the water concentration of the surface of the negative electrode active material layer is within a range from 142 ppm to 488 ppm.