Polymeric compositions and filled TPO articles having improved aesthetics

1. A polymeric composition comprising:

a. at least about 5 weight percent inorganic filler based on the total weight of the polymeric composition;

b. a high viscosity polypropylene impact copolymer having

i. a highly crystalline portion, wherein the highly crystalline portion is present from about 20 weight percent to about 90 weight percent of the high viscosity polypropylene impact copolymer, and

ii. a xylene soluble portion, wherein the xylene soluble portion is present from about 10 weight percent to about 80 weight percent of the high viscosity polypropylene impact copolymer, has a z-average molecular weight greater than about 1,500,000 Da, a number average molecular weight less than about 100,000 Da, and a polydispersity index greater than about 5; and

c. a low viscosity substantially linear ethylene polymer (SLEP) having a polydispersity index less than about 3.5, and a melt flow rate greater than about 40 g/10 min as measured according to ASTM D-1238 at 190° C./2.16 kg.

2. The polymeric composition of claim 1 , wherein the polymer composition is a polymeric masterbatch suitable for at-press blending with a polyolefin diluent to achieve a molded surface having low surface imperfections, and the concentration of the inorganic filler is at least about 35 weight percent based on the total weight of the polymeric masterbatch.

3. The polymeric masterbatch of claim 2 wherein the filler concentration is from about 35 weight percent to about 85 weight percent based on the total weight of the polymeric masterbatch.

4. The polymeric masterbatch of claim 3 wherein the filler comprises talc.

5. The polymeric masterbatch of claim 4 , wherein at least 90 weight percent of the filler has a median particle size from about 0.1 to about 20 μm.

6. The polymeric masterbatch of claim 2 , wherein the high viscosity polypropylene impact copolymer has a melt flow rate from about 0.4 to about 2.5 g/10 min as measured according to ASTM D-1238 at 230° C./2.16 kg.

7. The polymeric masterbatch of claim 2 , wherein the xylene soluble portion of the high viscosity polypropylene impact copolymer has a z-average molecular weight from about 1,800,000 Da to about 3,500,000 Da.

8. The polymeric masterbatch of 7 wherein the polymeric masterbatch has a xylene soluble component, wherein the xylene soluble component has a z average molecular weight greater than about 1,000,000 Da.

9. The polymeric masterbatch of claim 8 wherein the SLEP is selected from the group consisting of an ethylene-propylene copolymer, an ethylene-butene copolymer, an ethylene-hexene copolymer, an ethylene-octene copolymer, and any combination thereof, and the SLEP has a melt flow rate greater than about 150 g/10 min as measured according to ASTM D-1238 at 190° C./2.16 kg.

10. The polymeric masterbatch of claim 8 , wherein the high viscosity polypropylene impact copolymer has a melting temperature greater than about 140° C., and the xylene soluble portion is present at a concentration of 22 to about 55 weight percent based on the total weight of the polypropylene impact copolymer.

11. The polymeric masterbatch of claim 3 , wherein the xylene soluble portion of the high viscosity impact copolymer has a polydispersity index greater than about 7.

12. The polymeric masterbatch of claim 3 , wherein the polymeric masterbatch is in the form of pellets or granules.

13. The polymeric composition of claim 1 , wherein the polymeric composition is a filled thermoplastic polyolefin composition wherein

the inorganic filler is present at a concentration from about 5 to about 30 weight percent based on the total weigh of the filled thermoplastic polyolefin composition;

and the polymeric composition includes a low viscosity polypropylene having a melt flow rate greater than about 4 g/10 min as measured according to ASTM D-1238 at 230° C. and a melting temperature greater than about 130° C.

14. The filled thermoplastic polyolefin composition of claim 13 wherein the high viscosity propylene impact copolymer is present at a concentration from about 1 to about 8 weight percent based on the total weigh of the filled thermoplastic polyolefin composition.

15. The filled thermoplastic polyolefin composition of claim 13 wherein the SLEP is present at a concentration greater than about 1 weight percent based on the total weight of the filled thermoplastic polyolefin composition.

16. A filled thermoplastic polyolefin composition of claim 15 , wherein the composition further comprises a second SLEP having a melt flow rate less than about 35 g/10 min.

17. The filled thermoplastic polyolefin composition of claim 16 wherein the second SLEP is present at a concentration from about 3 to about 30 weight percent based on the total weight of the filled thermoplastic polyolefin composition.

18. The filled thermoplastic polyolefin composition of claim 13 wherein the low viscosity polypropylene is present at a concentration greater than about 30 weight percent based on the total weight of the filled thermoplastic polyolefin composition.

19. A process for manufacturing a molded article including at least one part having a masterbatch containing polymeric composition comprising the steps of:

a. melt blending at least 10 weight percent of a polymeric masterbatch of claim 2 , and at least 40 weight percent of a diluent polypropylene having a melt flow rate greater than about 2.5 g/10 min as measured according to ASTM D-1238 at 230° C./2.16 kg to form a molten blend of the masterbatch containing polymeric composition; and

b. molding the masterbatch containing polymeric composition.

20. The process of claim 19 wherein the step of melt blending occurs in the screw of an injection molding machine; the step of molding the masterbatch containing polymeric composition includes a step of molding the molten blend; and the process does not include a step of melt compounding the polymeric masterbatch and the diluent polypropylene prior to the melt blending step.