Metal-organic frameworks for Xe/Kr separation
Metal-organic framework (MOF) materials are provided and are selectively adsorbent to xenon (Xe) over another noble gas such as krypton (Kr) and/or argon (Ar) as a result of having framework voids (pores) sized to this end. MOF materials having pores that are capable of accommodating a Xe atom but have a small enough pore size to receive no more than one Xe atom are desired to preferentially adsorb Xe over Kr in a multi-component (Xe—Kr mixture) adsorption method. The MOF material has 20% or more, preferably 40% or more, of the total pore volume in a pore size range of 0.45-0.75 nm which can selectively adsorb Xe over Kr in a multi-component Xe—Kr mixture over a pressure range of 0.01 to 1.0 MPa.
1. A method of separating Xe and another noble gas in a gas mixture, comprising contacting the gas mixture with an adsorbent material comprising a metal-organic framework (MOF) material wherein the MOF material has 20% or more of the total pore volume of a size to receive no more than one Xe atom for selectively adsorbing Xe from the gas mixture;
wherein the MOF material has carboxylate linkers and wherein the MOF material has a chemical formula unit represented by Cu 2 (3,3′,5,5′-biphenyltetracarboxylate).
2. The method of claim 1 wherein selectivity of the MOF material for Xe from the gas mixture is about 9 to about 11 over a pressure range of 0.01 to 1.0 MPa at 273 K.
3. The method of claim 1 wherein the MOF material has 40% or more of the total pore volume in a pore size range of 0.45-0.75 nm.
4. The method of claim 1 wherein the other noble gas is selected from the group consisting of Kr and Ar.
5. The method of claim 1 wherein the MOF material exhibits a selectivity for Xe from the gas mixture of about 9 and 11 over a pressure range of 0.01 to 1.0 MPa at 273 K.