Film made from heterogenous ethylene/alpha-olefin interpolymer
A multilayer film is disclosed, having at least two layers. A first layer includes a first interpolymer of ethylene and at least one alpha-olefin. The first interpolymer has a density of less than 0.925 g/cm3, and an average M v and a valley temperature between the interpolymer and high crystalline fraction, T he , such that the average M v for a fraction above T he from ATREF divided by average M v of the whole polymer from ATREF (M hc /M hp ) is less than about 1.95 and the first interpolymer has a CDBI of less than 60%. At least one other second layer includes a second inter-polymer of ethylene and at least one alpha-olefin, the second interpolymer having a density from 0.925 to 0.965 g/cm3. The interpolymer of ethylene and at least one alpha-olefin can have a high density fraction and an overall density such that % HD fraction <0.0168x2−29.636x+13036 where x=density in g/cm3.
1. A multilayer film comprising at least two layers a first layer and a second layer; and
wherein a first layer consists of a first heterogeneously branched ethylene/α-olefin interpolymer and optionally a low density polyethylene, wherein said first heterogeneously branched ethylene/α-olefin interpolymer comprises an interpolymer fraction and a high crystalline fraction, and wherein the first heterogeneously branched ethylene/α-olefin interpolymer has a density in the range of from 0.917 to 0.922 g/cm 3 , and a molecular weight distribution M w /M n in the range from 3.5 to 5, and an average Mv and a valley temperature between the interpolymer fraction and the high crystalline fraction, T hc , such that the average Mv for the fraction above the T hc from ATREF divided by the average Mv of the whole polymer from ATREF (M hc /M hp ) is less than 1.7, and wherein the first heterogeneously branched ethylene/α-olefin interpolymer has a CDBI of less than 60%, and wherein the ATREF profile has one valley between the interpolymer fraction and the high crystalline fraction; and
wherein at least one other second layer consists of a second heterogeneously branched ethylene/α-olefin interpolymer selected from LLDPE or HDPE, wherein the second interpolymer has a density from 0.925 to 0.965 g/cm 3 ; and
wherein the first heterogeneously branched ethylene/α-olefin interpolymer is prepared in at least one reactor at a reactor temperature from about 160° C. to about 180° C., and at a Al/Ti molar ratio from 1.5 to about 2.5:1
wherein the film has thickness of about 120 microns and a Dart (B) measured using ASTM D1709 of at least 250 grams, a percent haze measured according to ASTM D1003 of less than 16 percent, and a 2 percent secant modulus calculated by (MD+CD)/2 measured in accordance with ASTM D882 of at least 240 MPa.
2. The film of claim 1 , wherein said first heterogeneously branched ethylene/α-olefin interpolymer has a CDBI of less than 55%.
3. The film of claim 1 , wherein said second heterogeneously branched ethylene/α-olefin interpolymer has melt index in the range between 0.1 to 10 g/10 minutes.
4. The film of claim 1 , wherein the first heterogeneously branched ethylene/α-olefin interpolymer has a melt index from about 0.1 to about 10 g/10 min.
5. The film of claim 1 , wherein the first heterogeneously branched ethylene/α-olefin interpolymer comprises long chain branches less than 1 per 1000 C atoms.
6. The film of claim 1 , wherein the second heterogeneously branched ethylene/α-olefin interpolymer comprises a molecular weight distribution, Mw/Mn, of less than about 5.
7. The film of claim 1 , wherein the first heterogeneously branched ethylene/α-olefin interpolymer has been at least partially crosslinked to at least 5%, by weight, gel.
8. A fabricated article comprising the film of claim 1 .