Sialon sintered body and cutting insert
The present invention provides a technique of improving wear resistance of a Sialon sintered body. The Sialon sintered body has a Sialon phase including at least a β-Sialon and a 12H-Sialon among an α-Sialon, the β-Sialon and the 12H-Sialon. A ratio of a second Sialon total content, which is a sum of the contents of the α-Sialon and the 12H-Sialon, to a first Sialon total content, which is a sum of contents of the α-Sialon, the β-Sialon and the 12H-Sialon, is greater than 20% and not greater than 55%, and a ratio of the content of the 12H-Sialon to the first Sialon total content is not less than 2% and not greater than 55%.
1. A Sialon sintered body having a Sialon phase comprising at least a β-Sialon and a 12H-Sialon among an α-Sialon, the β-Sialon and the 12H-Sialon,
wherein a ratio of a second Sialon total content to a first Sialon total content is greater than 20% and not greater than 55%, and a ratio of the content of the 12H-Sialon to the first Sialon total content is greater than 5% and not greater than 55%, wherein the first Sialon total content is a sum of contents of the α-Sialon, the β-Sialon and the 12H-Sialon and the second Sialon total content is a sum of the contents of the β-Sialon and the 12H-Sialon, wherein the ratio of the content of the α-Sialon to the first Sialon total content is not less than 0% and not greater than 15%.
2. The Sialon sintered body in accordance with claim 1 , wherein the ratio of the second Sialon total content to the first Sialon total content is greater than 20% and not greater than 50%, and the ratio of the content of the 12H-Sialon to the first Sialon total content is greater than 5% and not greater than 50%.
3. The Sialon sintered body in accordance with claim 1 , wherein the ratio of the second Sialon total content to the first Sialon total content is not less than 21% and not greater than 46%, and the ratio of the content of the 12H-Sialon to the first Sialon total content is greater than 5% and not greater than 46%.
4. The Sialon sintered body in accordance with claim 1 , wherein the ratio of the content of the α-Sialon to the first Sialon total content is greater than 0% and not greater than 15%, and the ratio of the content of the 12H-Sialon to the first Sialon total content is greater than 5% and not greater than 30%.
5. The Sialon sintered body in accordance with claim 1 , wherein the β-Sialon represented by a formula Si 6-z Al Z O Z N 8-Z has a Z value of greater than 0.7 and smaller than 1.5.
6. The Sialon sintered body in accordance with claim 1 , wherein yttrium is contained either in particles of the α-Sialon or in an interparticle phase present between particles of the respective Sialons included in the Sialon phase.
7. A cutting insert, comprising the Sialon sintered body in accordance with claim 1 .