Method for producing porous film or tape of expanded polytetrafluoroethylene supporting catalyst particles, and ozone-removing filter
An improved method for producing an expanded polytetrafluoroethylene (PTFE) porous film or tape supporting catalyst particles. The method for producing an expanded PTFE porous film or tape supporting catalyst particles according to the invention comprises a step of preparing tape-like porous PTFE, a step of impregnating the tape-like porous PTFE with a solution or dispersion of catalyst particles, a step of substantially removing the solvent or dispersing medium, and a step of further stretching the tape-like porous PTFE containing the catalyst particles in the machine direction (MD) and/or the transverse direction (TD).
1. A method for producing an expanded PTFE porous film or tape supporting catalyst particles, said method comprising:
impregnating a porous polytetrafluoroethylene (PTFE) tape with a dispersion of catalyst particles within a dispersing medium,
removing the dispersing medium, and
stretching the porous PTFE tape containing the catalyst particles in a machine direction (MD), a transverse direction (TD), or in both the machine and transverse directions.
2. The method according to claim 1 , further comprising forming said polytetrafluoroethylene tape, said forming comprising:
extrusion molding a paste of polytetrafluoroethylene (PTFE) fine powder into an extruded tape;
drying said extruded tape; and
stretching said dried extruded tape to form said porous polytetrafluoroethylene tape.
3. The method according to claim 2 , wherein said stretching occurs in the machine direction (MD) or in the both machine direction (MD) and the transverse direction (TD) after said drying.
4. The method according to claim 1 , wherein a total draw ratio in the TD is in the range of 1.5-300.
5. The method according to claim 1 , wherein a total draw ratio in the MD is in the range of 1.2-200.
6. The method according to claim 1 , wherein the catalyst particles comprise at least one ozonolytic catalyst selected from the group consisting of manganese dioxide, copper oxide, titanium dioxide, platinum, palladium, alumina and combinations thereof.
7. An ozone-removing filter comprising an expanded PTFE porous film supporting ozonolytic catalyst particles produced by the method according to claim 1 ,
wherein the catalyst particles comprise at least one ozonolytic catalyst selected from the group consisting of manganese dioxide, copper oxide, titanium dioxide, platinum, palladium, alumina and combinations thereof.
8. The method according to claim 1 , wherein said dispersing medium comprises a member selected from the group consisting of ethanol, propanol, hexane and water.