Branched organopolysiloxanes
View Patent ↗The invention relates to branched organopolysiloxanes and to their preparation and use. A branched organopolysiloxane is prepared by the reaction of an alkoxysilane with a substantially linear organopolysiloxane containing at least one hydroxyl or hydrolysable group bonded to silicon, in the presence of a phosphazene catalyst. The branched organopolysiloxanes obtained can be suitable for use in a moisture curable sealant composition capable of curing to a high modulus seal, with less tendency to gel than when using other siloxane polycondensation catalysts. Phosphazene catalysts also have the advantage that the content of undesired low molecular weight cyclic silicones in the polymerization product is low.
1. A process for the preparation of a branched organopolysiloxane comprising reacting an alkoxysilane with a substantially linear organopolysiloxane containing at least one hydroxyl or hydrolysable group bonded to silicon, wherein the reaction is carried out in the presence of a phosphazene catalyst and a diluent selected from a hydrocarbon oil comprising from 5 to 25 carbon atoms per molecule, where the amount of diluent used in the process is 5 to 70% of the combined weight of alkoxysilane, substantially linear organopolysiloxane and diluent.
2. The process according to claim 1 wherein the substantially linear organopolysiloxane has terminal hydroxyl groups bonded to silicon.
3. The process according to claim 1 wherein the alkoxysilane comprises a trialkoxysilane of the formula R′Si(OR) 3 , where R represents an alkyl group having 1 to 4 carbon atoms and R′ represents a monovalent hydrocarbon or substituted hydrocarbon group having 1 to 18 carbon atoms.
4. The process according to claim 1 wherein the alkoxysilane comprises a tetraalkoxysilane.
5. The process according to claim 1 wherein the alkoxysilane comprises a partially condensed alkoxysilane containing on average more than two alkoxy groups per molecule bonded to silicon.
6. The process according to claim 1 wherein the phosphazene catalyst is a perchlorooligophosphazenium salt of the formula
[Cl 3 P—(N═PCl 2 ) n Cl] + Z −
where n has an average value in the range 1 to 10 and Z represents an anion of the formula MX v+1 in which M is an element having an electronegativity on Pauling's scale of from 1.0 to 2.0 and valency v and X is a halogen atom.
7. The process according to claim 1 wherein the phosphazene catalyst is an oxygen-containing chlorophosphazene of the formula Cl(PCl 2 ═N) n —P(O)Cl or HO(PCl 2 ═N) n —P(O)Cl 2 where n has an average value in the range 1 to 10.
8. The process according to claim 1 wherein the phosphazene catalyst is an oxygen-containing chlorophosphazene containing organosilicon radicals and has the formula R″ 3 SiO(PCl 2 ═N) n —P(O)Cl 2 where each R″ represents a monovalent hydrocarbon or substituted hydrocarbon group having 1 to 18 carbon atoms and n has an average value in the range 1 to 10.
9. The process according to claim 1 wherein the diluent is a natural oil.