Fibrous sheet that disintegrates in water, process for manufacturing said fibrous sheet, core consisting of strips of said fibrous sheet
A fibrous sheet having a basis weight of between 20 and 1000 g/m2 that disintegrates in water, has 10% to 70% starch on the basis of the total weight of the dry fibrous sheet. The disintegration time in water, measured in accordance with standard NF Q34-020 applied to a specimen of the sheet of 9×8 cm 2 , is less than 50 seconds. A loss of strength of the sheet measured in accordance with a defined table test corresponds to a loss of strength of a specimen of said sheet forming an angle of at least 85° after having being wetted with water for a duration of 6 seconds, and/or a residual wet strength of the sheet relative to its dry strength, as measured according to a defined ring crush test, is less than 1%. The fibrous sheet may be used for the manufacture of a water disintegrable core in a roll of tissue paper.
1. A process for manufacturing a fibrous sheet comprising at least 30% of papermaking fibres, that disintegrates in water in less than 120 seconds, the process comprising the steps of:
preparing a pulp by suspending the fibres in water;
adding to the pulp a starch which is not soluble in water at a temperature at which it is incorporated;
forming the fibrous sheet from the pulp containing the starch on a forming table; and
drying the fibrous sheet at a temperature that progressively rises so as to reach complete gelatinization of the starch,
wherein the starch is uniformly distributed through the thickness of the fibrous sheet including the external surfaces of the sheet.
2. A process for manufacturing a fibrous sheet comprising at least 30% of papermaking fibres, that disintegrates in water in less than 120 seconds, the process comprising the steps of:
preparing a pulp by suspending the fibres in water;
forming the fibrous sheet from the pulp;
adding to the fibrous sheet a starch which is not soluble in water at a temperature at which it is incorporated, wherein the water-insoluble starch is incorporated when the sheet is on a forming wire; and
drying the fibrous sheet containing the starch at a temperature that progressively rises so as to reach complete gelatinization of the starch.
3. The process according to claim 1 , further comprising pressing the fibrous sheet before the drying step.
4. The process according to claim 1 , wherein the water-insoluble starch is a starch modified by physical, chemical or physico-chemical treatment.
5. The process according to claim 2 , further comprising pressing the fibrous sheet before the drying step.
6. The process according to claim 2 , wherein the water-insoluble starch is a starch modified by physical, chemical or physico-chemical treatment.