Alginate-based building materials
The present disclosure describes various building materials used in the building and construction industry, and to buildings or objects constructed therefrom, and to methods of making these building materials. The building materials comprise a polymeric material, such as sodium alginate and/or calcium alginate which confers significant flame-, fire- and heat-resistance or imperviousness to the materials. Other substances can be added to the materials to improve cross-linking and/or to produce resistance to fungal degradation. The building materials which can be produced, processed, or treated using the alginate polymers of the invention include, but are not limited to, wood products; masonry products; wall, roofing, flooring and siding products; and paint products. Further, sodium alginate in the form of a gel may be used as a firebreak to effectively stop the advance of grass fires, wildfires, and forest fires.
1. A method of producing a building material product, comprising:
providing a construction material matrix component;
providing an alginate polymer component comprising sodium alginate;
combining the construction material matrix component and the alginate polymer component; and
processing the combined construction material matrix component and alginate polymer component to form the building material product, wherein the building material product comprises 0.5% to 25% by weight alginate polymer component, based upon the total weight of the combined construction material matrix component and alginate polymer component taken as 100% by weight; and wherein said processing includes exposing the combined construction material matrix component and alginate polymer component to calcium, wherein the sodium alginate is thereby converted to calcium alginate in the building material product.
2. The method of claim 1 , wherein the alginate polymer component further comprises a cross-linking agent, wherein the cross-linking agent is at least one of a xanthan gum, a carrageenan, an agar, a cellulose gum, a pectin, a pectin resin, a locust bean gum, a locust bean resin, a xanthan gum resin, a sodium salt of carrageenan, a gellan gum, a gellan gum resin, a whey protein gum, a whey protein resin, a propylene glycol, an Arabic gum, an Arabic gum resin, a guar gum, a guar gum resin, a gum tragacanth, and a gum ghatti.
3. The method of claim 1 , wherein the building material product is selected from the group consisting of an alginate-treated wood product, masonry product, paint product, siding product, flooring product, and roofing product.
4. The method of claim 1 , wherein the construction material matrix component is saw dust, stranded wood, wood chips, or a mixture thereof, and said processing further comprises pressing the combined construction material matrix component and alginate polymer component into a pressed board.
5. The method of claim 4 , wherein said pressed board contains no external adhesives or bonding agents.
6. The method of claim 4 , wherein said exposing comprises pouring a solution of calcium halide onto said combined construction material matrix component and alginate polymer component prior to said pressing.
7. The method of claim 1 , wherein the construction material matrix component is wood lumber, said combining comprises immersing the construction material matrix component in the alginate polymer component, and said processing further comprises applying vacuum pressure to the combined construction material matrix component and alginate polymer component prior to said exposing.
8. The method of claim 7 , wherein said exposing comprises applying a solution of a calcium halide to the combined construction material matrix component and alginate polymer component under vacuum.
9. The method of claim 1 , wherein the construction material matrix component is a mixture of sand, water, and masonry mortar comprising said calcium, and wherein the building product is a masonry product.
10. The method of claim 9 , wherein said masonry product is flexible and when formed into a ½-inch thick slab shows a deflection of approximately ⅛-inch.
11. The method of claim 1 , wherein the construction material matrix component is paint, said combined construction material matrix component and alginate polymer component being an alginate-treated paint, said method further comprising applying said alginate-treated paint to a substrate surface after said combining, wherein said exposing comprises applying a solution of a calcium halide to said alginate-treated paint on said substrate surface.
12. The method of claim 11 , wherein said alginate-treated paint has a dry time of less than 15 minutes after said exposing.
13. The method of claim 12 , wherein said alginate-treated paint has a dry time of less than 60 seconds after said exposing.
14. The method of claim 1 , wherein the construction material matrix component is selected from the group consisting of:
(a) saw dust, stranded wood, wood chips, or a mixture thereof;
(b) wood lumber;
(c) cement;
(d) concrete
(e) paint;
(f) gypsum;
(g) glass;
(h) clay;
(i) asphalt;
(j) fiberglass;
(k) stone;
(l) brick;
(m) mortar; and
(n) grout.
15. The method of claim 1 , wherein the construction material matrix component is saw dust, stranded wood, wood chips, or a mixture thereof, said building product being a pressed board having no external adhesives or bonding agents.
16. The method of claim 1 , wherein the product is resistant to catching fire when the flame of a torch having a temperature of about 1000° C. is held to the surface of the product for between 10 to 60 minutes.