METHOD FOR PREPARING POLYAMIDE FOAM AND FOAM CAPABLE OF BEING PRODUCED BY SAID METHOD
A method for preparing polyamide foam is described. Polyamide foam produced according to the method is also described. A method including heating a composition including at least one polyamide and at least one polyurethane, and stabilizing the resulting cellular structure is also described. Use of a composition including at least one polyamide and at least one polyurethane for preparing polyamide foam is also described.
1 . A process for the preparation of a polyamide foam, the process comprising at least the following stages:
a) heating a composition comprising at least the following compounds:
A: a polyamide
B: a polyurethane
optionally C: a compound comprising at least one acid functional group
at a temperature greater than or equal to the melting point of the polyamide A of the composition, and
b) stabilizing the cellular structure obtained.
2 . The process as claimed in claim 1 , wherein the polyamide is a polymer with a number-average molecular weight of greater than or equal to 10 000 g/mol.
3 . The process as claimed in claim 1 , wherein the polyurethane exhibits a number-average molecular weight of greater than or equal to 2000 g/mol.
4 . The process as claimed in claim 1 , wherein the polyamide is a linear polyamide.
5 . The process as claimed in claim 1 , wherein the polyamide is selected from the group consisting of polyamide 6, polyamide 6,6, polyamide 6,10, blends thereof and copolymers thereof.
6 . The process as claimed in claim 1 , wherein the polyamide is polyamide 6,6.
7 . The process as claimed in claim 1 , characterized in that wherein the composition comprises 0.5% to 20% by weight, of polyurethane, with respect to the weight of polyamide and polyurethane of the composition.
8 . The process as claimed in claim 1 , wherein stage b) is obtained physically.
9 . A foam obtained by the process as claimed in claim 1 .
10 . An article obtained by shaping the foam obtained by the process as claimed in claim 1 .
11 . A method of preparing a polyamide foam, the method comprising preparing the foam with a composition described in claim 1 .
12 . The method as claimed in claim 11 , wherein the composition is in the form of expandable granules.
13 . The process as claimed in claim 1 , wherein at least one acid functional group in the compound C is a carboxylic acid functional group.
14 . The process as claimed in claim 2 , wherein the number-average molecular weight is greater than or equal to 14,000 g/mol.
15 . The process as claimed in claim 2 , wherein the number average molecular weight is greater than or equal to 17,000 g/mol.
16 . The process as claimed in claim 3 , wherein the number-average molecular weight is greater than or equal to 5,000 g/mol.
17 . The process as claimed in claim 3 , wherein the number-average molecular weight is greater than or equal to 10,000 g/mol.
18 . The process as claimed in claim 3 , wherein the composition comprises 1% to 10% by weight of polyurethane.