Solution Derived Nanocomposite Precursor Solutions, Methods for Making Thin Films and Thin Films Made by Such Methods
Solution derived nanocomposite (SDN) precursor solutions are disclosed that comprise one or more metal precursors that are dissolved in a liquid comprising polar protic and polar aprotic solvents. The precursor solutions are characterized by the formation of a gel after a shear force is applied to the precursor solution or to a thin layer of precursor solution. Also disclosed are methods using such precursor solutions to make thin films, thin films made using the precursor solutions, thin films having a minimum surface area and devices containing thin films as disclosed herein.
1 . A precursor solution comprising one or more sol-gel metal precursors and/or sol-gel metalloid precursors, a polar protic solvent and a polar aprotic solvent, wherein said precursor solution forms a gel after a shear force is applied to said precursor solution and said polar aprotic solvent is present in said solution at between about 1 and 25 vol %.
2 . The precursor solution of claim 1 wherein the viscosity of said solution increases with increasing shear force.
3 . The precursor solution of claim 1 wherein the metal in said one or more sol-gel metal precursors is selected from the group consisting of transition metals, lanthanides, actinides, alkaline earth metals, and Group IIIA through Group VA metals.
4 . The precursor solution of claim 1 wherein the metalloid in said one or more sol-gel metalloid precursors is selected from the group consisting of boron, silicon, germanium, arsenic, antimony, tellurium, bismuth and polonium.
5 . The precursor solution of claim 1 wherein said one or more sol-gel metal precursors are metallic compounds selected from the group consisting of organometallic compounds, metallic organic salts and metallic inorganic salts.
6 . The precursor solution of claim 5 wherein said organometallic compound is a metal alkoxide.
7 . The precursor solution of claim 6 wherein said metal alkoxide is selected from the group consisting of methoxides, ethoxides, propoxides butoxides and phenoxides.
8 . The precursor solution of claim 5 wherein said metallic organic salt is selected from the group consisting of formates, acetates and propionates.
9 . The precursor solution of claim 5 wherein said metallic inorganic salt is selected from the group consisting of halide, hydroxide, nitrate, phosphate and sulfate.
10 . The precursor solution of claim 1 wherein said polar protic solvent is selected from the group consisting of organic acids and organic alcohols.
11 . The precursor solution of claim 10 wherein said organic acid is selected from the group consisting of formic acid, acetic acid, propionic acid and butyric acid.
12 . The precursor solution of claim 10 wherein said organic alcohol is selected from the group consisting of methyl alcohol, ethyl alcohol, propyl alcohol and butyl alcohol.
13 . The precursor solution of claim 1 wherein said polar aprotic solvent is selected from the group consisting of halogenated alkyl, alkyl ether, alkyl esters, ketones, aldehydes, alkyl amides, alkyl amines, alkyl nitriles and alkyl sulfoxides.
14 . The precursor solution of claim 1 wherein said halogenated alkyl polar aprotic solvent is selected from the group consisting of dichloromethane, 1,2-dichloroethane, 1,2-dichloropropane, 1,3-dichloropropane, 2,2-dichloropropane, dibromomethane, diiodomethane and bromoethane.
15 . The precursor solution of claim 13 wherein said alkyl ether polar aprotic solvent is selected from the group consisting of tetrahydrofuran, methyl cyanide and acetonitrile.
16 . The precursor solution of claim 13 wherein said ketone polar aprotic solvent is selected from the group consisting of acetone, methyl isobutyl ketone and ethyl methyl ketone.
17 . The precursor solution of claim 13 wherein said alkyl amide polar aprotic solvent is selected from the group consisting of dimethyl formamide, dimethyl phenylpropionamide, dimethyl chlorobenzamide and dimethyl bromobenzamide.
18 . The precursor solution of claim 13 wherein said alkyl amine polar aprotic solvent is selected from the group consisting of diethylenetriamine, ethylenediamine, hexamethylenetetramine, dimethylethylenediamine, hexamethylenediamine, tris(2-aminoethyl)amine, ethanolamine, propanolamine, ethyl amine, methyl amine, (1-2-aminoethyl)piperazine.
19 . The precursor solution of claim 13 wherein said alkyl nitrile aprotic solvent comprises acetonitrile.
20 . The precursor solution of claim 13 wherein said alkyl sulfoxide aprotic solvent is selected from the group consisting of dimethyl sulfoxide, diethyl sulfoxide and butyl sulfoxide.
21 . The precursor solution of claim 1 wherein at least one of said metal or metalloid precursors is an organometallic or organometalloid compound comprising a polymerizable organic moiety.
22 . The precursor solution of claim 1 further comprising polymerizable organic monomer, organic oligomer or organic polymer.
23 . The precursor solution of any of claim 1 further comprising a photo-inducible polymerization catalyst.
24 . The precursor solution of claim 23 wherein said photo-inducible polymerization catalyst is selected from the group consisting of titanocenes, benzophenones/amines, thioxanthones/amines, bezoinethers, acylphosphine oxides, benzilketals, acetophenones, and alkylphenones.
25 . The precursor solution of claim 1 further comprising an acid or base catalyst.
26 . A process for making a solid thin film layer comprising the step of applying the precursor solution of claim 1 to one or more surfaces of a substrate wherein said applying provides sufficient shear force to cause gelation of said precursor solution to form a gelled thin layer.
27 . The process of claim 26 further comprising exposing said gelled thin layer to UV, visible or infrared radiation.
28 . The process of claim 27 wherein said exposing causes formation of a solid thin film.
29 . The process of claim 28 wherein said exposing raises the temperature of said solid thin film so as to form a crystalline structure.
30 . The process of claim 26 wherein said applying is by dip coating, spin coating or a combination of both.
31 . The process of claim 26 wherein said applying is by roll coating or roll to roll coating.
32 . A thin film made according to the process of claim 26 .
33 . A thin film having a thickness from 1 to 500 nanometers and a surface area of at least 50 cm 2 .
34 . A device comprising a thin film having a thickness from 1 to 500 nanometers and having a surface area of at least 50 cm 2 .