Thermal barrier coating system with porous tungsten bronze structured underlayer
A system of layers in a protective coating ( 20 ) for a substrate ( 22 ), including at least an outer thermal barrier layer ( 32 ) and a tungsten bronze structure ceramic underlayer ( 30 ) that reduces spalling of the outer layer. The range of materials for the underlayer includes ceramics of the form Ba 6−3m Re 8+2m Ti 18 O 54 , where 0<m<1.5, and Re is any rare earth element or mixture thereof. These underlayer materials reduce spalling of the thermal barrier layer, and thus extend the life of the coating system. In some embodiments, materials for the outer thermal barrier layer may include Yttria-stabilized Zirconia (YSZ) or ceramics with lower thermal conductivity than YSZ. A segmented YSZ layer ( 26 ) is provided in some embodiments for additional thermal expansion compliance.
1. A thermal barrier coating comprising:
an underlayer of a tungsten bronze structured ceramic material; and
a layer of a thermal barrier material on the underlayer;
wherein the underlayer comprises at least one of the group of: 1) an underlayer material Ba 6−3m RE 8+2m Ti 18 O 54 where 0<m<1.5, and RE represents any rare earth element or mixture thereof; and 2) an underlayer material Ba Nd 2 Ti 4 O 12 with rare earth dopants that reduce its thermal conductivity;
wherein the thermal barrier material comprises 7-9 mol. % yttria-stabilized zirconia (YSZ) or a ceramic with a lower thermal conductivity than the YSZ; and
wherein the underlayer is 25% to 35% porous, and the layer of thermal barrier material is 25% to 35% porous.
2. The thermal barrier coating of claim 1 , further comprising a bond coat on a substrate, and a segmented layer on the bond coat, wherein the underlayer is disposed on the segmented layer.
3. The thermal barrier coating of claim 1 , wherein the ceramic with lower thermal conductivity comprises 25-65 mol % Ytterbium Zirconate, 25-65 mol % Gadolinium Zirconate, or 25-65 mol % Gadolinium Hafnate.
4. The thermal barrier coating of claim 1 , further comprising a bond coat on a substrate, and a segmented layer of greater than 95% dense yttria-stabilized zirconia on the bond coat, wherein the underlayer is disposed on the segmented layer.
5. The thermal barrier coating of claim 1 , comprising the following sequence of layers;
a bond coat on a substrate;
a segmented layer comprising YSZ on the bond coat;
a third layer of porous YSZ on the segmented layer; and
the underlayer on the third layer.
6. The thermal barrier coating of claim 5 , wherein the ceramic with lower thermal conductivity comprises 25-65 mol % Ytterbium Zirconate, 25-65 mol % Gadolinium Zirconate, or 25-65 mol % Gadolinium Hafnate.
7. The thermal barrier coating of claim 1 , comprising the following sequence of layers:
a bond coat on a substrate;
a segmented layer comprising YSZ on the bond coat; and
the underlayer on the segmented layer.
8. The thermal barrier coating of claim 7 , wherein the ceramic with lower thermal conductivity comprises 25-65 mol % Ytterbium Zirconate, 25-65 mol % Gadolinium Zirconate, or 25-65 mol % Gadolinium Hafnate.
9. The thermal barrier coating of claim 1 , comprising the following sequence of layers:
a bond coat on a substrate;
a third layer of 8-15% porous YSZ on the bond coat; and
the underlayer being on the third layer.
10. The thermal barrier coating of claim 9 , wherein the ceramic with lower thermal conductivity comprises 25-65 mol % Ytterbium Zirconate, 25-65 mol % Gadolinium Zirconate, or 25-65 mol % Gadolinium Hafnate.
11. The thermal barrier coating of claim 1 , comprising the following sequence of layers;
a bond coat on a substrate; and
the underlayer being on the bond coat.
12. The thermal barrier coating of claim 11 , wherein the ceramic with lower thermal conductivity comprises 25-65 mol % Ytterbium Zirconate, 25-65 mol % Gadolinium Zirconate, or 25-65 mol % Gadolinium Hafnate.
13. A thermal barrier coating comprising:
an underlayer comprising Ba (Nd 1.2 Sm 0.4 Gd 0.4 ) Ti 4 O 12 ; and
a layer of a thermal barrier material on the underlayer.