Modification of wood-based lignocellulosic material
View Patent ↗Porous wood-based lignocellulosic material is modified by incorporating into its pore matrix a bonded silica filling. An immobilized-silica precursor such as a water-glass solution of silica subunits or a colloidal silica is used to produce the filling, such as by immersion of the lignocellulosic material therein. The impermeable wood-based lignocellulosic material produced thereby is inflammable and impermeable to penetration by fluids and pests.
1. A method for modifying porous wood-based lignocellulosic material having a pore matrix filled with a pore-matrix fluid comprising:
incorporating a bonded silica filling into said pore matrix of said lignocellulosic material by the steps of
displacing pore-matrix fluid by charging a fluid immobilized-silica precursor to said pore matrix, said fluid immobilized-silica precursor consisting essentially of a fluid carrier and an immobilized silica precursor selected from the group consisting of a water-glass solution of silica subunits and a colloidal silica within a particle-size range of from 10 to 80 Angstrom units; and
then curing said immobilized-silica precursor to provide a silica filling bonded to said pore matrix.
2. A method for modifying porous wood-based lignocellulosic material having a pore matrix according to claim 1 wherein said fluid carrier is water.
3. A method for modifying porous wood-based lignocellulosic material having a pore matrix according to claim 1 wherein said immobilized-silica precursor is a combination of a plurality of monodispersed colloidal silicas each within a particle-size range of from 10 to 80 Angstrom units.
4. A method for modifying porous wood-based lignocellulosic material having a pore matrix according to claim 1 wherein said colloidal silica is charged to said pore matrix by ambient-pressure immersion of said lignocellulosic material in said colloidal silica.
5. A method for modifying porous wood-based lignocellulosic material having a pore matrix according to claim 1 wherein said colloidal silica is charged to said pore matrix by pressurized immersion of said lignocellulosic material in said colloidal silica.
6. A method for modifying porous wood-based lignocellulosic material having a pore matrix according to claim 1 wherein said charging is a combination of an ambient-pressure immersion and a pressurized immersion.
7. A method for modifying porous wood-based lignocellulosic material having a pore matrix according to claim 1 wherein said charging is a plurality of cycles of immersion followed by curing.
8. A method for modifying porous wood-based lignocellulosic material having a pore matrix according to claim 1 wherein said curing is an air drying to constant weight.
9. A method for modifying porous wood-based lignocellulosic material having a pore matrix according to claim 1 wherein said curing is an elevated-temperature drying to constant weight.
10. A method for modifying porous wood-based lignocellulosic material having a pore matrix according to claim 1 wherein said porous wood-based lignocellulosic material is corrugated cardboard.