Cementitious mortar and method for improved reinforcement of building structures
Cementitious mortar with improved characteristics for forming structures incorporating synthetic fibres, in particular in the form of webs, for reinforcing building structures. The mortar comprises a methylmethacrylate/n-butylacrylate copolymer resin and glass filaments dispersed in the mortar. The invention also relates to a reinforcement method for building structures, using said mortar.
1. A cementitious mortar consisting of:
(a) 5% to 89.595% of a cement,
(b) 10% to 70% of an inert mineral filler having a particle dimension less than 700 microns,
(c) 0.05% to 2.5% of at least one additive selected from the group consisting of a fluidifying additive and a superfluidifying additive,
(d) 0.005% to 1% of a thixotropic additive of a cellulose class,
(e) 0.3% to 24% of a methylmethacrylate/n-butylacrylate copolymer resin, and
(f) 0.05% to 30% of a glass filament dispersed in the mortar, the glass filament having a length of 1 to 30 mm and a diameter of 5 to 100 microns, and
(g) a laurylsulphonic acid compound in an amount of up to 1.5%,
the percentages being by weight referred to the total weight of the cementitious mortar.
2. The mortar of claim 1 , wherein the glass filament (f) has a length of 3 mm to 24 mm and a diameter of 8 microns to 85 microns.
3. The mortar of claim 1 , wherein the methylmethacrylate/n-butylacrylate copolymer resin (e) is present in an amount of 0.5% to 18% by weight.
4. The mortar of claim 1 , wherein the glass filament (f) is present in an amount of 0.4% to 23% by weight.
5. The mortar of claim 1 which is suitable for forming a structure incorporating a web comprising a synthetic fiber, wherein the synthetic fiber comprises at least one selected from the group consisting of a glass fiber, a carbon fiber, a polymer fiber, and a poly[benz(1,2-D:5,4-D′)bisoxazole-2,6-diyl-1,4-phenylen] fiber.
6. The mortar of claim 1 , wherein the glass filament (f) is an alkali resistant glass filament.
7. The mortar of claim 1 , wherein the glass filament (f) has a length of 3 mm to 24 mm and a diameter of 8 microns to 85 microns.
8. The mortar of claim 1 , wherein the cement (a) is present in an amount of 20% to 70% by weight.
9. The mortar of claim 1 , wherein the cement (a) is at least one cement selected from the group consisting of a Portland cement, a composite Portland cement, a blast furnace cement, a pozzolan cement, and a composite cement.
10. The mortar of claim 1 , wherein the additive (c) is a fluidifying additive.
11. The mortar of claim 1 , wherein the additive (c) is a superfluidifying additive.
12. The mortar of claim 1 , wherein the additive (c) is an acrylic superfluidifier.
13. The mortar of claim 1 , wherein the thixotropic additive (d) is at least one selected from the group consisting of methylcellulose, methyl hydroxyethyl cellulose, methylhydroxypropylcellulose, hydroxyethyl cellulose, hydroxypropylcellulose, carboxymethylcellulose, and carboxymethylhydroxyethylcellulose.
14. The mortar of claim 1 , wherein the thixotropic additive (d) is present in an amount of 0.015% to 0.65% by weight.
15. The cementitious mortar of claim 1 , wherein
the cement (a) is a Pozzolan cement present in an amount of from 6.80 to 87.28%,
the inert mineral filler (b) is quartz having a dimension of 0.1-0.35 mm,
the thixotropic additive is methylcellulose in an amount of 0.006-0.9%,
the fluidifying additive is an acrylic present in an amount of from 0.05-2.4%,
the methylmethacrylate/n-butylacrylate copolymer resin is present in an amount of 0.5-24%, and
the glass filament (f) is present in an amount of 0.075-27%.
16. The cementitious mortar according to claim 1 , consisting of:
(a) from 6.80 to 87.28% of the cement,
(b) from 10.79 to 68.40% of the inert mineral filler,
(c) from 0.05 to 2.40% of an acrylic superfluidifying additive,
(d) from 0.01 to 0.9% of the thixotropic additive,
(e) from 0.5 to 23.90% of the copolymer resin, and
(f) from 0.08 to 27% of the glass filament.
17. The cementitious mortar of claim 16 , wherein the cement is Pozzolan cement, the inert filler is silica fume, the superfluidifying additive is acrylic superfluidifier, and the thixotropic additive is methylcellulose.
18. The cementitious mortar of claim 1 , to which an ether lauryl sulphonate is added in an amount of from 0.25-1.5% and the cement (a) is present in an amount of 5-89.345%.