Aqueous composition for enteric hard capsule, method of preparing enteric hard capsule, and enteric hard capsule prepared using the method
An aqueous composition for an enteric hard capsule, a method of preparing an enteric hard capsule, and an enteric hard capsule prepared using the method. The aqueous composition for an enteric hard capsule includes an enteric base material, a capsule forming aid, and a neutralizing agent. The method of preparing an enteric hard capsule includes: preparing an aqueous composition by dissolving an enteric base material, a capsule forming aid, and a neutralizing agent in water; preheating the aqueous composition to a temperature that is less than the gelation temperature for the aqueous composition; immersing a mold pin heated to a temperature that is greater than the gelation temperature for the aqueous composition into the aqueous composition; taking the mold pin out of the aqueous composition to obtain a film formed on the mold pin; and maintaining the film at a temperature that is equal to or greater than the gelation temperature for the aqueous composition for a predetermined period of time to fix the film on the mold pin and drying the film.
1. A method of preparing an enteric hard capsule, the method comprising:
preparing an aqueous composition by dissolving an enteric base material, a capsule forming aid, and a neutralizing agent in water and maturing the aqueous composition at room temperature;
preheating the aqueous composition to a first temperature that is less than a gelation temperature for the aqueous composition;
immersing a mold pin heated to a second temperature that is greater than the gelation temperature for the aqueous composition into the aqueous composition;
taking the mold pin out of the aqueous composition to obtain a film formed on the mold pin; and
preparing a capsule shell by maintaining the film at a third temperature that is equal to or greater than the gelation temperature for the aqueous composition for a first time period to fix the film on the mold pin and drying the film at a fourth temperature for a second time period,
wherein the enteric base material is selected from the group consisting of hydroxypropyl methylcellulose phthalate (HPMCP) and hydroxypropyl methylcellulose acetate succinate (HPMCAS),
wherein the capsule forming aid is cellulose ether selected from the group consisting of hydroxypropyl methylcellulose (HPMC) and methylcellulose (MC),
wherein the neutralizing agent is a basic compound,
wherein an amount of the neutralizing agent is in a range of 1 to 5% based on a total weight of the aqueous composition; and wherein an amount of the enteric base material is in a range of about 8 to about 25% based on the total weight of the aqueous composition, an amount of the capsule forming aid is in a range of about 1 to about 12% based on the total weight of the aqueous composition; wherein the first temperature is less than the gelation temperature for the aqueous composition by about 4 to about 12.0° C.; wherein the second temperature is greater than the gelation temperature for the aqueous composition by about 10 to about 31° C.;
wherein the third temperature is in a range of about 60 to about 80° C., and the first time period is in a range of about 1 to about 15 minutes; wherein the fourth temperature is in a range of about 20 to about 40° C., and the second time period is in a range of about 30 to about 60 minutes.